The mechanical and electrical properties of the hot-pressed and annealed $\beta$-SiC+39vol. %ZrB2 electroconductive ceramic composites were investigated by adding 1, 2, 3wt% Al2O3+Y2O3(6:4wt%) of the liquid forming additives. In this microstructures, no reactions were observed between $\beta-SiC$ and ZrB2. The relative density is over 90.8% of the theoretical density and the porosity decreased with increasing Al2O3+Y2O3 contents. Phase analysis of the composites by XRD revealed $\alpha-SiC(6H, 4H)$, ZrB2 and $\beta-SiC$(15R). Flexural srength showed the highest of 315.5MPa for composites added with 3wt% Al2O3+Y2O3 additives as room temperature. Owing to crack deflection and crack bridging of fracture toughness mechanism, the fracture toughness showed 5.5MPa.m1/2 and 5.3MPa.m1/2 for composites added with 2wt% and 3wt% Al2O3+Y2O3 additives respectively at room temperature. The area fraction of the elongated SiC grain in the etched surface of sample showed 65% and 65.1% for composite added with 2wt% and 3wt% Al2O3+Y2O3 additives respectively. The electrical resistivity at room temperature. The electrical resistivity of the composites wall all positive temperature coefficient(PTCR) against temperature up to $700^{\circ}C$.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1997년도 춘계학술발표회논문집(2)
• /
• pp.195-200
• /
• 1997

핵융합로 증식재용 r-LiAlO$_2$, Li$_2$ZrO$_3$, Li$_2$TiO$_3$ 분말을 자발착화 연소반응법으로 합성하였다. LiAlO$_2$와 달리 Li$_2$ZrO$_3$ 와 Li$_2$TiO$_3$는 가열하는 동안 침전물이 생겼지만 카르복실산기만을 지닌 구연산과 아민기만을 지닌 우레아를 화학정량의 조성으로 혼합한 연료로 쉽게 분말을 합성할 수 있었다. LiAlO$_2$나 Li$_2$TiO$_3$분말은 별도의 하소 공정이필요없이 원하는 결정상이 형성되었으며, Li$_2$ZrO$_3$분말은 Li이 과량인 상이 형성되므로 110$0^{\circ}C$에서 하소하여 원하는 상을 얻었다. 합성된 Li계 산화물 분말은 비표면적 10~17 $m^2$/g으로 약 150 nm정도의 입자크기를 갖는 미세한 입자이었다.

• 한국공작기계학회논문집
• /
• 제11권3호
• /
• pp.86-92
• /
• 2002

In this study, experiments were carried out to investigate the characteristics of grinding and wear process of diamond wheel far ceramic materials. Normal component of grinding resistance of $Al_2$O$_3$ was less then that of $Si_3 N_4$ and $ZrO_2$. This seems to be the characteristics of ceramic tools on work pieces both of high hardness. For the case of $Si_3 N_4$ and $ZrO_2$, as the mesh number of wheel increases, the surface roughness decreases. For the case of $Al_2 O_3$, the surface roughness does not decreases. Specific binding energy decreases as the material removal rate per unit time increases. For the case of $Si_3 N_4$ and $ZrO_2$, grinding is carried out by abrasive wear processes. For the case of $Al_2 O_3$, grinding is carried out by grain shedding process due to brittle fracture.

• 한국세라믹학회지
• /
• 제20권4호
• /
• pp.289-296
• /
• 1983

The Wetting of fusion cast $Al_2O_3$ brick and $Al_2O_3 -ZrO_2$ brick by liquid Ag was studied by the sessile drop technique in Ar atmosphere. In this experiment the specimens were photographed per 2$0^{\circ}C$with increasing temperature from 96$0^{\circ}C$ melting point of Ag. And the method of photographing was carried out by shadow technique. The cosine of the contact angle increased linearly with increasing temperature in both systems. And the relation between the cosine of the contact angle and the temperature was Cos$\theta$=1.132+$0.75{\times}10^{-3}T$ for $Al_2O_3$ brick and Cos$\theta$=-1.706+$1.125{\times}10^{-3}T$ for $Al_2O_3 -ZrO_2$ brick In both systems the contact angle decreased as the surface of substrate became smoother. The work of adhesion which was 503.5ergs/$cm^2$ for $Al_2O_3$brick and 393.6 ergs/cm2 for $Al_2O_3 -ZrO_2$ brick at 96$0^{\circ}C$ increased parabolically with increasing temperature in both system.

• 한국재료학회지
• /
• 제15권7호
• /
• pp.453-457
• /
• 2005

Piezoelectric properties of $Pb(Mn_{1/3}Nb_{2/3})O_3-PbZrO_3-PbTiO_3$ ceramics were investigated with $Al_2O_3$ content $(0.0-1.0 wt\%)$. The constituent phases, microstructure, electromechanical coupling factor, dielectric constant, piezoelectric charge and voltage constants were analyzed. Diffraction peaks for (002) and (200) planes were identified by X-ray diffractometer for all the specimens doped with $Al_2O_3$, indicating the MPB (morphotropic phase boundary) composition of tetragonal structures. The highest sintered density of $7.8 g/cm^3$ was obtained for $0.2wt\%\;Al_2O_3-doped$ specimen. Grain size increased by doping $Al_2O_3$ up to $0.3 wt\%$, and it decreased by more doping. Electromechanical coupling factor, dielectric constant, piezoelectric charge and voltage constants increased by doping $Al_2O_3$ up to $0.2wt\%$, and it decreased by more doping. This might result from the formation of oxygen vacancies due to defects in $O^{2-}$ ion sites and the substitution of $Al^{3+}$ ions.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 추계학술대회 논문집 학회본부 C
• /
• pp.847-849
• /
• 1998

The effect of $Al_{2}O_{3}$ additives on the microstructure, mechanical and electrical properties of ${\beta}$-SiC+39vol.%$ZrB_2$ electroconductive ceramic composites by pressureless sintering were investigated. The ${\beta}$-SiC+39vol.%$ZrB_2$ ceramic composites were pressureless sintered by adding 4, 8, 12wt.% $Al_{2}O_{3}$ powder as a liquid forming additives at $1950^{\circ}C$ for 1h. Phase analysis of composites by XRD revealed mostly of $\alpha$-SiC(6H), $ZrB_2$ and weakly $\alpha$-SiC(4H), $\beta$-SiC(15R) phase. The relative density of composites was lowered by gaseous products of the result of reaction between $\beta$-SiC and $Al_{2}O_{3}$ therefore, porosity was increased with increased $Al_{2}O_{3}$ contents. The fracture toughness of composites was decreased with increased $Al_{2}O_{3}$ contents, and showed the maximum value of $1.4197MPa{\cdot}m^{1/2}$ for composite added with 4wt.% $Al_{2}O_{3}$ additives. The electrical resistivity of ${\beta}$-SiC+39vol.%$ZrB_2$ electroconductive ceramic composite was increased with increased $Al_{2}O_{3}$ contents, and showed positive temperature coefficient resistance (PTCR) in the temperature from $25^{\circ}C$ to $700^{\circ}C$.

• 한국수소및신에너지학회논문집
• /
• 제16권1호
• /
• pp.49-57
• /
• 2005

[ $MO/Al_2O_3-ZrO_2$ ](M=Ni and Cu) mixed metal oxides were prepared using sol-gel method in order to investigate the applicability to the 2-step thermo-chemical water splitting process and their redox behaviors were studied by temperature programmed reaction(TPR) from room temperature to 900$^{\circ}C$ under 5% $H_2$/Ar for the reduction and $H_2O$/Ar for the oxidation, respectively. From the results, peaks of the reduction and the oxidation on temperature were shifted with the change of crystalline phases due to the addition of $Al_2O_3$ and $ZrO_2$. The intensities of the peaks were also increased with the increase of contents of NiO or CuO that could be considered as active species. In addition, based on the observation of SEM images before and after the redox test, it seemed that $Al_2O_3-ZrO_2$ added prevented high temperature sintering of active metal components such as Ni (or Cu) on the surface and played a role of dispersing the active species homogeneously in solid solution of mixed oxides.

• 한국세라믹학회지
• /
• 제30권1호
• /
• pp.1-6
• /
• 1993

Dielectric and piezoelectric porperties of pseudoternary xPb(Al2/3W1/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 (x=1~10mol%) ceramic system have been investigated as a function of the amount of PAW[Pb(Al2/3W1/3)O3] and sintered from 110$0^{\circ}C$ to 120$0^{\circ}C$ for 1hr. As the amount of PAW increases, the c/a of tetragonal structure decreases. The grain size was reduced with increasing the amount of PAW addition. However, the density, dielectric constant and electromechanical coupling factor(kp) exhibited a maximum value at the amount of 5mol% PAW addition.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.84.2-84.2
• /
• 2000

• Bulletin of the Korean Chemical Society
• /
• 제34권11호
• /
• pp.3387-3390
• /
• 2013

Catalytic gasification of mandarin waste residue was carried out using direct and indirect catalyst-contact methods for the first time. In the indirect method, non-catalytic reaction in a reactor was followed by catalytic upgrading of vapor product in another reactor. Two different catalysts, $Ni/{\gamma}-Al_2O_3$ and $Ni/CeO_2-ZrO_2$, were employed. $CeO_2-ZrO_2$ support was prepared using hydrothermal synthesis in supercritical water. The catalysts were characterized by $H_2$-temperature programmed reduction and Brunauer-Emmett-Teller analyses. Under the condition of equivalent ratio (ER) = 0, the indirect catalyst-contact method led to a higher gas yield than the direct method. Under ER = 0.2, the yield of biogas obtained over $Ni/CeO_2-ZrO_2$ was higher than that obtained over $Ni/{\gamma}-Al_2O_3$. Also, the coke formation of $Ni/CeO_2-ZrO_2$ was lower than that of $Ni/{\gamma}-Al_2O_3$. Such results were attributed to the higher reducibility and better lattice oxygen mobility of $Ni/CeO_2-ZrO_2$, which were advantageous for partial oxidation reaction.