Specimens of Ti-10Ta-10Nb have been tested for Rockwall hardness after heating to either the $\alpha$+$\beta$ and $\beta$-phase field. And the specific heat and the dilatometer of Ti-10Ta-103Nb swaged have been measured. From the result, the $\beta$ transus of the alloy was determined to be 82$0^{\circ}C$. The hot deformation behavior of Ti-10Ta-10Nb with an $\alpha$+$\beta$ microstructure is modeled in the temperature 75$0^{\circ}C$ and strain rate range 0.001-10$^{-1}$

• Korean Journal of Materials Research
• /
• v.11 no.2
• /
• pp.132-136
• /
• 2001

Iron- silicide has been produced by mechanical alloying process and consolidated by hot pressing. As-consolidated iron silicides were consisted of $\beta$-FeSi$_2$ phase, and untransformed mixture of $\alpha$-$Fe_2Si_5$ and $\varepsilon$-FeSi phases. Isothermal annealing has been carried out to induce the transformation to a thermoelectric semiconducting $\beta$-$FeSi_2$ phase. The condition for $\beta$-FeSi$_2$ transformation was investigated by utilizing DTA, SEM, TEM and XRD analysis. The phase transformation was shown to be taken place by a vacuum isothermal annealing at $830^{\circ}C$ for 24 hours. The mechanical and thermoelectric properties of $\beta$-FeSi$_2$ materials before and after isothermal annealing were characterized in this study.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.99-104
• /
• 1998

40$0^{\circ}C$ $H_2O$ steam 분위기에서 Zr-2,5wt%Nb 및 Zr-20wt%Nb 합금의 산화거동을 열처리조건에 따른 미세조직 관점에서 고찰하였으며, 형성된 oxide를 분석하여 산화기구를 규명하고자 하였다. Zr-Nb 합금의 산화거동은 열처리에 따라 협성된 조직상에 매우 민감하였는데, 주 조직인 a-Zr 상 보다는 $\beta$상들에 ($\beta$-Zr, $\beta$-Nb) 보다 큰 영향을 받는 것으로 보인다. $\beta$-Zr 상은 $\alpha$-Zr 상에 비해 부식저항성이 낮으며, 그 양에 관계없이 유사한 정도의 부식거동을 보인다. $\beta$-Nb 상의 경우, 미세한 크기로 적은양이 존재하는 경우 부식저항성에 별다른 영향이 없어 보이는 반면, 상당량의 $\beta$-Nb 상이 조대한 크기로 (약 0,2$\mu\textrm{m}$) 존재하는 경우 매우 불안정한 부식거동을 보였다. 이들 $\beta$상들의 낮은 산화저항성은 Nb$_2$O$_{5}$ 을 포함한 Nb 계 oxide의 형성에 주로 기인한 것으로 추정된다.

• Applied Biological Chemistry
• /
• v.45 no.2
• /
• pp.108-113
• /
• 2002

The compositions of essential oils isolated from the aerial parts of Chrysanthemum boreale and C. indicum by steam distillation were analyzed by GC and GC-MS. Ninty-four components were identified in the essential oil from C. boreale, with camphor (15.40% as GC peak area), cir-chrysanthenol (14.11%), ${\alpha}-thujone$ (13.27%), 1,8-cineole (4.16%), ${\alpha}-pinene$ (3.80%), ${\beta}-caryophyllene$ (3.58%), gremacrene D (2.69%), camphene (2.40%), umbellulone (2.24%) and ${\beta}-pinene$ (2.00%) as the major constituents. In the oil from C. indicum, the major constituents among 80 components identified were germacrene D (16.50%), camphor (10.04%), ${\alpha}-thujone$ (6.40%), ${\alpha}-pinene$ (4.50%), ${\alpha}-cadinol$ (3.97%), camphene (3.82%), ${\beta}-pinene$ (3.67%), zingiberene (3.64%), cis-chrysanthenol (3.45%), piperitone (3.09%), 1,8-cineole (2.61%) and chrysanthenone (2.42%). The oil from C. boreale, although similar to that from C. indicum in many respects, contained proportionately higher levels of camphor, cis-chrysanthenol, ${\alpha}-thujone$, 1,8-cineole and umbellulone, while that from C. indicum contained higher levels of germacrene D, ${\beta}-caryophyllene$, ${\alpha}-cadinol$, zingiberene, cis-chrysanthenol and piperitone.

• Journal of Technologic Dentistry
• /
• v.27 no.1
• /
• pp.9-17
• /
• 2005

The use of titanium alloys as biomaterials is increasing due to their superior biocompatibility and enhanced corrosion resistance compared to conventional stainless steels and cobalt-based alloys. Ti-6Al-4V ($\alpha+\beta$type) alloy instead of pure titanium ($\alpha$type) is being widely used as biomaterials has some characteristics such as high fatigue strength, tensile strength and corrosion resistance. But it has been reported recently that the vanadium element expresses cytotoxicity and the aluminium element is related with dementia of Alzheimer type and neurotoxicity. In order to overcome their detrimental effects, $\beta$-phase stabilizer Nb was chosen in the present study. This paper was described the influence of phase changes of Ti-Nb alloys on mechanical properties. Ti-3wt.%Nb($\alpha$type),Ti-20wt.%Nb($\alpha+\beta$type) and Ti-40wt.%Nb($\beta$type) alloys were melted by vacuum arc furnace. The specimens were homogenized at 1050$^{\circ}C$ for 24hr and were then hot rolled to 50% reduction. Each alloys were solution heat treated at $\beta$ zone and $\alpha+\beta$ zone after homogenization and then were aged. The mechanical properties of Ti alloys were analysed by hardness test, tensile test, elongation test and SEM test. The results can be summarized as follows: 1) The higher hardness value of $\alpha+\beta$type alloy was obtained compared to the, $\alpha,\beta$type alloys. 2) The aged treated showed better hardness compared to the solution heat treated, homogenized. 3) In the case of solution and aging treatment at $\beta$region, the $\alpha+\beta$type alloy showed the most highest tensile strength and $\beta$type alloy showed the best elongation.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.658-664
• /
• 1997

The effect of metal oxides($K_2O, MgO, CaO,Al_2O_3$, and $TiO_2$) on the kinds of pure $SiO_2$ phase, and $SiO_2$ phases in the composition of vitreous porcelain body was investigated. Also, the effect of the ratio $SiO_2$ to $Al_2O_3$ in the composition of porcelain body with stabilized of cristobalite phase was investigated. In the case of the addition of $K_2O, MgO, CaO, Al_2O_3$, and $TiO_2$ to pure $SiO_2$, the major phase was $\alpha$-cristobalite, $\alpha$-cristobalite, $\alpha$-quartz, $\alpha$-quartz and amorphous, respectively. As the ratio of $SiO_2$ to $Al_2O_3$ in the composition of porcelain body was decreased, the stabilization of cristobalite phase was promoted and only the critical value of $SiO_2/Al_2O_3$ ratio that stabilizing the cristobalite phase in it was 68.10/22.75. The addition of $K_2$O, MgO, CaO,Al_2O_3$, and $TiO_2$ to the composition of porcelain body stabilized already did not affect on the formation of $\alpha$-cristobalite phase which degraded the thermal properties of porcelain body, and suppressed the formation of a, $\beta$-cristobalite.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.4
• /
• pp.343-350
• /
• 1995

A Abstract Systematic studies of the effects of crystalline forms of starting powders and p processing variables on the texture of hot - pressed silicon carbide are described. The results I indicate that hot - pressing of $\beta$ - SiC can produce strong textures and composite type duplex microstructure due to the ${\beta} {\rightarrow} {\alpha}$ phase transformation of SiC. The texture variations d during post - annealing have been observed. In the case of using a - SiC as starting pow¬d ders, the degree of preferred orientation by hot - pressing is relatively weak.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.23-23
• /
• 1996

• Journal of the Korean Ceramic Society
• /
• v.29 no.3
• /
• pp.232-240
• /
• 1992

Densification behavior, microstructural evolution, and mechanical properties of hot-pressed specimens using $\beta$-SiC and $\alpha$-SiC powder with Al2O3 additive were studied. Beta-SiC powder was fully densified as 205$0^{\circ}C$, but $\alpha$-SiC powder was at 210$0^{\circ}C$. The maximum flexural strength and the fracture toughness of the specimen hot-pressed using $\beta$-SiC powder were 681 MPa and 6.7 MPa{{{{ SQRT {m } }}, and thosevalues of specimen hot-pressed using $\alpha$-SiC powder were 452 MPa and 4.7 MPa{{{{ SQRT {m } }}, respectively. The strength superiority of specimen hot-pressed using $\beta$-SiC powder was due to the finer grain size, and higher density. The higher toughness of specimen hot-pressed using $\beta$-SiC powder than $\alpha$-SiC powder than $\alpha$-SiC powder was due to the crack deflection mechanism arised from the difference of thermal expansion coefficient between $\alpha$ and $\beta$-SiC phases which were co-existed in the sintered body.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.5 no.5
• /
• pp.484-489
• /
• 2004

Isolation of phycobiliprotein from S. platensis was performed by using $30-60{\%}$ ammomium sulfate fractionation, Sephadex G-100 gel filtration and DEAE-Sephacel anionic exchange chromatography. Isolated phycobiliprotein was determined to be a c-phycocyanin with a maximum absorption wavelength at 620 nm. This phycobiliprotein consisted of $({\alpha}$ and $({\beta}$ subunit when analyzed through SDS-PAGE. The molecular weights of $({\alpha}$ and $({\beta}$ subunit were 14.5 kDa and 16 kDa, respectively. The native molecular weight of phycobiliprotein through gel filtration was about 100 kDa. These results show that the structure of phycobiliprotein from S. platensis might be aggregated form of $({\alpha}{\beta})_{3}-trimer$.