• Journal of the Korean Ceramic Society
• /
• v.28 no.11
• /
• pp.935-941
• /
• 1991

Effects of calcination process and ZrO2 addition on the electrical properties of [(Ba0.82Sr0.08Ca0.1)O]m(Ti1-$\chi$Zr$\chi$)O2 ceramics have been investigated. With the variation of A/B-site ratio m of the dielectric formulations, sintering behavior and the resistivity after sintering in a reducing atmosphere have been affected by the calcination process. When the dielectric formulations of m=1.01 were sintered in a reducing atmosphere, the room-temperature resitivity of 109 {{{{ OMEGA }}.cm was obtained for samples processed with two-step calcination, which was much lower than 1012 {{{{ OMEGA }}.cm of samples calcined once. It was confirmed that high resistivity of Ca-doped BaTiO3 ceramics, after sintering in a reducing atmosphere, is maintained by acceptor-like behavior of CaTi" which is formed by Ca substitution to Ti-site. It was also found out that the critical amount of B-site Ca substitution for reduction inhibition of BaTiO3 is around 0.005 mol. With the increasing amount of ZrO2 addition to dielectric formulations, Curie peak was depressed and Curie temperature was lowered due to the enhanced diffuse phase transition.tion.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.34-37
• /
• 2001

In this study, the capacitance-voltage properties of $(Sr_{1-x}\cdot Ca_x)TiO_3(0.05{\leq}x{\leq}0.20)$-based grain boundary layer ceramics were investigated. The ceramics were fabricated by the conventional mixed oxide method. The sintering temperature and time were $1480\sim1500^{\circ}C$ and 4 hours. respectively. The 2nd phase formed by the thermal diffusion of CuO from the surface leads to very excellent dielectric properties, that is, ${\varepsilon}_r$ >50000, tan$\delta$ <0.05, ${\Delta}C$ < ${\pm}10%.$ The capacitance is almost unchanged below about 20[V] but it decreases slowly about 20[V]. The results of the capacitance-voltage properties indicated that the grain boundary was composed of the continuous insulating layers.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1350-1355
• /
• 1999

Sintering characteristics and dielectric properties of low temperature sinterable Glass/Ceramic dielectric materials were investigated. The dielectric materials which were developed for microwave frequency applications consist of SiO2-TiO2-Bi2O3-RO system(RO:BaO-CaO-SrO) crystallizable glass and Al2O3 as a ceramic filler. Sintering experiments showed that no more densification occurred above 80$0^{\circ}C$ and bulk density and shrinkage depended on Al2O3 content only. Results of dielectric measurements showed that $\varepsilon$r Q$\times$f and $\tau$f of the material containing 30wt% Al2O3 were 17.3, 600 and +23 ppm respectively. Those values for 45 and 60wt% Al2O3 samples were 11.6, 1400, +0.7 ppm and 7.2, 2000, -8.5 ppm, repectively. The results clearly showed that the Glas/Ceramic materials of present experiment decreased in $\varepsilon$r and increased in $\times$f value and changed from positive to negative value in $\tau$f value with the increasement of Al2O3 content.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11b
• /
• pp.329-337
• /
• 2005

Synroc which comprises hollandite-rich ($Ba_{1-x}Cs_{2x}\;(Al_yTi_{2-y})\;Ti_{6}O_{16},\;75wt\%$), perovskite ($Ca_{1-x}Sr_xTiO_3,\;15wt\%$) and rutile ($TiO_2,\;10wt\%$) is devised for the immobilization of Sr/Cs (1:3, wt$\%$) separated from HLW liquid. Especially, hollandite-rich Synroc with different contents of Al element is fabricated, and its mineral phase assemblage and microstructure are determined by using XRD and SEM/EDS. The durability test is carried out by using MCC-1 method, leachate is analyzed by using ICP/MS and ICP/ AES. The results indicate that hollandite-rich Synroc variants is a suitable host for Immobilization of Sr/Cs separated from HLW liquid.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.37-43
• /
• 1999

Co-firing incompatibility between the low temperature sinterable Glass/ceramic and Ag-thick film was studied. The dielectric material, which has been developed for microwave frequency applications, consists of $SiO_2-TiO_2-Bi_2O_3$-$Bi_2O_3$-RO system(RO:BaO -CaO-SrO) crystallizable glass and $Al_2O_3$as a ceramic filler. The large camber in the sintered specimen and cracks at the Ag-film under the influence of the camber occurred due to the difference of densification rate between the ceramic sheet and the Ag-film $B_2O_3$addition to the Glass/ceramic mixture reduced the severe camber. The cambers decreased with increasing the $B_2O_3$ content, and completely disappeared with 14 vol% $B_2O_3$addition. With additions of $B_2O_3$, $\varepsilon_{r}$ decreased abruptly, Q$\times$f value increased largely and the $\tau_f$ value of the material quickly shifted to positive one.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.12
• /
• pp.1610-1616
• /
• 1995

The (Sr$_{1-x}$ .Ca$_{x}$)TiO$_{3}$(0.05.leq.x.leq.0.2) ceramics were fabricated to form semiconducting ceramics by sintering at about 1350[.deg. C] in a reducing atmosphere (N$_{2}$ gas). After being fired in a reducing atmosphere, metal oxides, CuO, was painted on the both surface of the specimens to diffuse to the grain boundary. They were annealed at 1100[.deg. C] for 2 hours. The 2nd phase formed by thermal diffusing from the surface lead to a very high apparent dielectric constant. The results of the capacitance-valtage measurements indicated that the grain boundary was composed of the continuous insulating layers. The capacitance is almost unchanged below about 20[V], but decreased slowly over 20[V]. The conduction mechanism of the specimens observed in the temperature range of 25~125[.deg. C], and is divided into three regions having different mechanism as the current increased: the region I below 200[V/cm] shows the ohmic conduction. The region II between 200[V/cm] and 2000[V/cm] can be explained by the Poole-Frenkel emission theory, and the region III above 2000[V/cm] is dominated by the tunneling effect.ct.

• Proceedings of the KIEE Conference
• /
• 1994.11a
• /
• pp.215-218
• /
• 1994

Dielectric properties of $(Sr_{l-x}{\cdot}Ca_x)_mTiO_3+0.006Nb_2O_5$($0.05{\leq}x{\leq}0.2$, 0.996$N_2$) were painted on the surface with CuO paste, and then annealed at $1100^{\circ}C$ for 2hr. Grain size increased with increasing substitutional contents of Ca up to 15[mol%], but decreased with further substitution. In the specimens with $10{\sim}15[mol%]$ of Ca and m=1, excellent dielectric properties were obtained as follows; dielectric constant <25000, dielectric loss($tan{\delta}[%]$) <0.3[%] and capacitance change rate with temperature <${\pm}10[%]$, respectively. All the specimens in this study exhibited dielectric relaxation with frequency as a function of the temperature. The dispersive frequency was over $10^6[Hz]$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.284-285
• /
• 2007

본 논문에서는 저소음 및 저 신호 왜곡 특성을 가지는 내환원성 유전체 원료를 개발하기 위하여 $(Ca_{0.7}Sr_{0.3})(Zr_{0.97}Ti_{0.03})O_3$에 $CaTiO_3$, $SrTO_3$, $BaTiO_3$를 첨가하여 이에 따른 유전 특성을 조사하였다. 첨가량의 조절 및 glass frit 첨가를 통하여 환원성 분위기에서도 유전율 80 ~ 100, 절연저항 (R*C) 500[ohm-F] 이상의 유전특성을 얻었다. 본 연구결과로 얻어진 유전재료를 적용하면 무소음 및 저 신호 왜곡 특성을 가지면서도 고 신뢰성의 MLCC를 제작할 수 있을 것으로 예상된다.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.2
• /
• pp.49-52
• /
• 2009

Barium strontium calcium titanate powders were prepared with the sol-gel method. Ferroelectric $(Ba_{0.54}Sr_{0.36}Ca_{0.1})TiO_3$(BSCT) thick films were fabricated by the screen-printing method on alumina substrate. Then we investigated the structural and dielectric properties of the BSCT thick films at different sintering temperatures. The thermal analysis showed that the BSCT polycrystalline perovskite phase formed at around $660^{\circ}C$. The X-ray diffraction analysis showed a cubic perovskite structure with no second phase present in all of the BSCT thick films. The average grain size and the thickness of the specimens sintered at $1450^{\circ}C$ were about $1.6{\mu}m$ and $45{\mu}m$, respectively. The relative dielectric constant increased and the dielectric loss decreased as the sintering temperature was increased; for BSCT thick films sintered at $1450^{\circ}C$ the values of the dielectric constant and the dielectric loss were 5641 and 0.4%, respectively, at 1 kHz.

• Electrical & Electronic Materials
• /
• v.10 no.2
• /
• pp.97-104
• /
• 1997

In this paper, in order to investigate the behavior of charged particles on (Sr.Ca)TiO$_{3}$ ceramics with paraelectric properties, the characteristics of electrical conduction and thermally stimulated current was measured respectively. As a result, the conduction mechanism is divided into three regions having different mechanism as the current increased. The region I below 200[V/Cm] shows the ohmic conduction. The region B between 200[V/cm] and 2000[V/cm] can be explained by the Poole-Frenkel emission theory, and the region III above 2000[V/cm] is dominated by the tunneling effect. The three peaks of TSC were obtained at the temperature of -20[.deg. C], 20[.deg. C] and 80[.deg. C], respectively. The origins of these peaks are that the .alpha. peak observed at -20[.deg. C] looks like to be ascribed to the ionization excitation from donor level in the grain, and the .alpha.' peak observed at 20 [.deg. C] appears to show up by hopping conduction of the trapped carrier of border between the oxidation layer and the grain, and the .betha. peak observed at 80[.deg. C] seems to be resulted from hopping conduction of existing carrier in the trap site of the border between the oxidation and second phase.