Ingot Casting with Ferro-Titanium Pretreatment Process using Ti Scrap

타이타늄 스크랩을 활용한 페로 -타이타늄 전처리 공정 적용 모합금 주조

  • Received : 2020.12.02
  • Accepted : 2021.01.22
  • Published : 2021.04.30
Download PDF
⟨ Previous Next ⟩

Abstract

A type of titanium alloy, ferro-titanium, is the main material used to manufacture steel and stainless steel. Considering economic aspects, ferro-titanium ingots are intended to be manufactured using low-cost titanium scrap, and the best pretreatment process for removing impurities from recycled titanium scrap surfaces was studied here. Instead of ordinary acid or organic solvents, ecofriendly methods were researched and applied, and chip scrap materials were used. A high-quality ferro-titanium ingot was manufactured from titanium scrap after a pretreatment process was applied, and the impurities and properties were analyzed and compared with commercial material standards through a component analysis.

타이타늄 합금 중 페로-타이타늄은 철강 업계에서 철강과 스테인리스강을 생산하는데 사용되는 주요 첨가물이다. 본 연구에서는 고품질의 페로-타이타늄 합금을 주조하기 위해 경제적인 면을 고려한 저비용 타이타늄 스크랩을 활용하고자 하였다. 먼저 재활용 타이타늄 스크랩의 표면에 형성되어 있는 절삭유 및 불순물을 제거하기 위한 최적의 전처리 공정을 연구하였다. 일반적인 세척 방법인 산이나 유기용제는 세척이 용이하나 환경적으로 문제가 되므로 친환경적인 방법을 고안하여 적용하고자 하였다. 또한, 타이타늄 스크랩을 활용하여 고품질의 페로-타이타늄 잉곳을 제조하고 성분 분석을 통해 불순물과 특성을 상용 소재 규격과 비교 분석하였다.

Keywords

Acknowledgement

본 연구는 산업통산자원부와 에너지기술평가원이 지원하는 에너지기술개발사업의 일환으로 수행되었습니다.

References

  1. G. Lutjering and J. C. Williams, "Titanium Chapter 10 - Special Properties and Applications of Titanium", Springer, Berlin (2007) 383.
  2. Lee YT, "Titanium", Steel & Metal Media, Korea (2009).
  3. Oh JM, Kwon H and Lim JW, Clean Tech., 19(2) (2013) 75. https://doi.org/10.7464/ksct.2013.19.2.075
  4. Oh JM, Lee BG, Cho WW, Lee SW, Choi GS, and Lim JW, Met. Mater. Int., 17(5) (2011) 733. https://doi.org/10.1007/s12540-011-1006-2
  5. G. Lutjering and J. C. Williams, "Titanium", Springer, Berlin (2003) 34.
  6. Oh JM, Lee BK, Suh CY and Lim JW, J. Alloy. Compd., 574 (2013) 1. https://doi.org/10.1016/j.jallcom.2013.04.041
  7. W. Gordon and A. Bennekom, Mater. Sci. Technol., 12 (1996) 126. https://doi.org/10.1179/mst.1996.12.2.126
  8. M. Panigrahi, R. K. Paramguru, R. C. Gupta, E. Shibata and T. Nakamura, High Temp. Mater. Proc., 29 (2010) 495. https://doi.org/10.1515/HTMP.2010.29.5-6.495
  9. Oh JM, Lee BK, Choi GS, and Lim JW, J. Korean Inst. Resource. Recycling, 21(1) (2012) 60.
  10. Lee JE, Cho NC, An CM, Noh JS and Moon JH, Clean Technology, 19(3) (2013) 264. https://doi.org/10.7464/ksct.2013.19.3.264