Abstract
The need for biodegradable plastic continues to increase, improvement of physical properties is necessary for actual use in the market. In this study, composite film was produced by adding peroxide additives to bioplastic according to concentration to investigate changes in the melt index, elongation, morphology, and TGA of the composite film. The addition of peroxide compatibilizer showed superior elongation of film and TGA compared to those of control. The added amount of compatibilizer affected the extrusion process, and it was revealed that adding an appropriate amount of peroxidizer is important. Analysis of the composite film's morphology revealed a heterogeneous dispersion sequence due to different rates of crystallization depending on the resin, and surface physical properties were best in the group added with 4% peroxide. The results above showed that the test group added with 4% peroxide compatibilizer was superior in the production of composite biodegradable film.
바이오플라스틱의 니즈는 계속 증가중이며 생분해 바이오플라스틱이 실제 현장에 사용되기 위해서는 물성개선이 필요한 실정이다. 본 연구에서는 바이오플라스틱에 과산화물 첨가제를 농도별로 첨가하여 생산한 복합화 필름의 신장율, morphology, TGA 변화를 조사하였다. 신장율과 TGA는 과산화물 상용화제 첨가구가 대조구 보다 더 우수한 것으로 나타났다. 상용화제 첨가량에 따라서 압출성형공정의 생산성에 영향을 미치며, 과산화물은 적정량을 첨가하는 것이 중요한 것으로 나타났다. 복합화 필름의 morphology를 분석한 결과 수지별로 결정화 속도가 달라이형분산배열을 관찰할 수 있었고, 표면물성은 4%의 과산화물 첨가구에서 가장 좋은 것으로 나타났다. 이상의 결과로부터 복합화 생분해 필름 제조 방법으로 과산화물 상용화제를 4% 첨가한 시험구가 우수한 것으로 사료되었다.