Structural and Luminescent Properties of Gd₂WO₆:RE³⁺ (RE = Dy, Sm, Dy/Sm) Phosphors for White Light Emitting Devices

백색광 소자 응용을 위한 Gd₂WO₆:RE³⁺ (RE = Dy, Sm, Dy/Sm) 형광체의 구조 및 발광 특성

A series of Dy³⁺, Sm³⁺, and Dy³⁺/Sm³⁺ doped Gd₂WO₆ phosphors were synthesized by the conventional solid-state reaction. The X-ray diffraction patterns revealed that all of the diffraction peaks could be attributed to the monoclinic Gd₂WO₆ crystal structure, irrespective of the type and the concentration of activator ions. The photoluminescence (PL) excitation spectra of Dy³⁺-doped Gd₂WO₆ phosphors contained an intense charge transfer band centered at 302 nm in the range of 240-340 nm and two weak peaks at 351 and 386 nm. Under an excitation wavelength of 302 nm, the PL emission spectra consisted of two strong blue and yellow bands centered at 482 nm and 577 nm. The PL emission spectra of the Sm³⁺-doped Gd₂WO₆ phosphors had a series of three peaks centered at 568 nm, 613 nm, and 649 nm, corresponding to the ⁶G_5/2 → ⁶H_5/2, ⁶G_5/2 → ⁶H_9/2, and ⁶G_5/2 → ⁶H_11/2 transitions of Sm³⁺, respectively. The PL emission spectra of the Dy³⁺- and Sm³⁺-codoped Gd₂WO₆ phosphors showed the blue and yellow emission lines originating from the ⁴F_9/2 → ⁶H_15/2 and ⁴F_9/2 → ⁴H_13/2 transitions of Dy³⁺ and reddish-orange and red emission bands due to the ⁴G_5/2 → ⁶H_7/2 and ⁴G_5/2 → ⁶H_9/2 transitions of Sm³⁺. As the concentration of Sm³⁺ increased from 1 to 15 mol%, the intensities of two PL spectra emitted by the Dy³⁺ ions gradually decreased, while those of the three emission bands due to the Sm³⁺ ions slowly increased, thus producing the color change from white to orange. The CIE color coordinates of Gd₂WO₆:5 mol% Dy³⁺, 1 mol% Sm³⁺ phosphors were (0.406, 0.407), which was located in the warm white light region.