초록
Mechanical components that support structures in aerospace and power generation industries require high-strength materials. Particularly, in the aerospace industry, aluminum alloys, titanium alloys, and composite materials are increasingly used due to their high maneuverability and durability to withstand low temperature extreme environments; however, ultra-high-strength steel is still used in key components under heavy loads such as landing gears. In this paper, the fault cause analysis and troubleshooting of aircraft parts made of ultra-high-strength steel (300M) broken during normal operation are described. To identify the cause of the defect, a temporary inspection of the same aircraft was performed, and material testing, non-destructive inspection, microstructure examination, and fracture area inspection of the damaged parts were performed. Fracture analysis results showed that a crack in the shape of a branch developed from the tool mark in the direction of the intergranular strain. Based on the results, the cause of fracture was confirmed to be stress corrosion.