Abstract
FCAW is used mainly in the welding of carbon steel and alloy steel because it can be welded in all positions and can obtain excellent quality at sites with variable working conditions. Recently, many studies in Korea have estimated the fatigue strength, residual stress, and deformation, and to develop a fillet welding process. On the other hand, there have been few studies of the mechanical properties based on the strength, macro and magnetic particle test results for fillet welding. This study shows the following results through fillet welding, macro testing and strength testing using SM490A (solid-structure rolled steel) for thick plates using SS400 (rolled steel) for the upper plate and FCAW. The hardness test, macro test and magnetic particle test were then conducted. The hardness tests showed that all result values were smaller than the KS B 0893 standard values of 350Hv. The macro-test showed that each type of welded part was in a normal organic state and that there were no internal errors, bubbles, or impurities on the front of the welded part. Therefore, there were no concerns about lamination. The magnetic particle examination showed no problems.
FCAW는 모든 자세에서 용접이 가능하고 작업여건 변수가 많은 현장에서 우수한 품질을 얻을 수 있는 장점이 있어 탄소강과 합금강의 중판, 후판 용접에 많이 사용되고 있다. 최근 국내에서 진행한 연구논문의 대부분이 피로 강도 평가 방법 연구, 잔류응력 및 변형, 필릿 용접 공정 개발 등의 연구가 시행되었으나 필릿 용접을 대상으로 경도, 매크로, 자분탐상 결과를 토대로 하여 기계적 특성을 나타낸 연구가 부족함에 따라 본 연구에서는 FCAW를 이용하여 상부는 SS400(일반구조용 압연강재) 후판은 SM490A(용접구조용 압연강재)를 이용하여 필릿 용접 후 경도시험, 매크로 시험, 자분탐상시험을 통해 아래와 같은 결론을 도출하였다. 경도시험 결과, 모든 결과 값이 KS B 0893의 규격치 350Hv보다 낮게 나타나 양호한 것으로 판단되었고, 매크로 시험 결과 용접부의 형상별로 균일한 조직 상태를 나타냈으며, 용접부 전 단면에 걸쳐 내부 결함, 기포 또는 불순물 등이 발견되지 않아 lamination의 우려가 없었으며, 자분탐상검사 결과 별도의 문제점이 발견되지 않았다.