Abstract
The purpose of this study was to evaluate the North Korea cement industry and technology status by comparing and analyzing the cement standards and properties of South and North Korea. In the literature study, data on North Korea's cement industry and standards were collected and analyzed through the Ministry of Unification's North Korea Data Center and other agency. The facilities, classification, and quality standards of South and North Korea cements were compared. In an experimental study, a survey on the quality of cement in North Korea was carried out through physical and chemical analysis experiments by obtaining a small amount of cement from North Korea, and compared with domestic cement. As a result, North Korea cement was of lower quality than South Korean cements. North Korea cement had lower C3S and higher C2S than South Korea cement, especially the residue content was much higher. In addition, North Korea cement had about 50% of the compressive strength of cement in South Korea because the clinker was not fired at a sufficient temperature due to the poor performance of the cement facilities in North Korea.
본 연구에서는 대표적인 건설재료인 시멘트를 대상으로 남북한의 시멘트 기준과 성능을 비교 분석하여 북한 시멘트 산업 및 기술 현황을 평가하는 것을 연구의 목적으로 문헌조사와 실험을 병행하였다. 문헌적 연구에서 북한의 시멘트 산업현황과 성능기준에 관한 자료를 통일부의 북한자료센터와 특수자료 취급기관 등을 통해서 수집하여 분석하였다. 이를 토대로 남북한 시멘트의 설비, 분류, 품질기준을 비교하였다. 실험적 연구에서 북한의 시멘트 품질에 관한 조사는 실제 북한의 시멘트를 중국을 통하여 소량 입수하여 물리화학 분석실험을 병행하였고 국내 시멘트와 비교분석을 하였다. 연구결과, 북한 시멘트는 한국 시멘트 보다 품질이 저하되는 것으로 나타났다. 북한 시멘트는 한국 시멘트 보다 C3S가 낮고 C2S가 높았으며, 특히 잔사 함량이 월등히 높게 나타났다. 또한 북한 시멘트는 한국의 시멘트보다 약 50% 정도의 압축강도 발현을 하지 못하였다. 이는 북한 시멘트 설비의 낙후 및 전력 문제로 인하여 충분한 온도로 클링커가 소성되지 않았기 때문인 것으로 사료된다.