Abstract
Oxygen-free copper (OFC) was prepared as a 90 mm cube and then processed with Multi-Axial Diagonal Forging - Initialization of Prior manufacturing History (MADF). The MADF process has been newly developed as a severe plastic deformation method. The MADF process consists of upset forging with a thickness reduction of 30% and diagonal forging with a diagonal angle of $135^{\circ}$. 1 cycle process consists of a 12 passes forging process. In order to analyze the characteristic changes according to the number of iterations, 1, 2, and 3 cycles of the MADF process were performed. The OFC specimens were MADF processed without surface cracks up to 3 cycles. The microstructure, hardness and tensile test of processed materials were analyzed to study the change of material properties according to the amount of MADF process. The results showed that the MADF process effectively refined the microstructure and increased the strength of OFC. In the case of specimens processed for more than 2 cycles, the grains of all measurement regions were refined to be less than $7{\mu}m$ of grain size. The 1 cycle MADF processed OFC showed the highest mechanical properties with the hardness of 132 HV and tensile strength of 395 MPa. Hardness and strength seemed to be saturated when processed over 2 cycles.