Abstract
$SnO_2$ was electrodeposited on nodule-type Cu foil at varing current density and electrodeposition time. Unlike the previous research results, when the anodic current is applied, the $SnO_2$ layer was not electrodeposited and the substrate is corroded. When the cathodic current was applied, the $SnO_2$ layer could be successfully deposited. At this time, the surface microstructure of the powdery type was observed, which showed similar crystallinity to amorphous and had a very large surface area. Crystallinity increased after low-temperature heat treatment at $250^{\circ}C$ or lower. As a result of evaluating the charge/discharge performances as an anode material for lithium ion battery, it was confirmed that the capacity of the heat treated $SnO_2$ was increased more than 2 times, but it still showed a limit point showing initial low coulombic efficiency and low cyclability. However, it was confirmed that the battery performances may be enhanced through optimizing the electrodeposition process and introducing post heat treatment.