Abstract
Froth flotation was performed to study the effect of phosphate addition in the experiment to remove As from tailing of Sang-dong Mine. The experiment without Trisodium phosphate (T.S.P) showed that the removal rate of As was 88.7% and weight-ratio of floating material was 2.52%. By contrast, the experiment with T.S.P showed that the removal rate of As was 92.74% and weight-ratio of floating material was 2.26%. In flotation without T.S.P, the average particle size of float material was 19.34 um and the amount less than 10um was 40.2%. On the other hand, in flotation with T.S.P the average particle size of float material was 176.8 um and the amount less than 10um was 6.5%. The result of X.R.F analysis presented that contents of $SiO_2$ was 42.74% in float material of the experiment without T.S.P. In contrast, contents of $SiO_2$ was 29.56% in float material of the experiment with T.S.P.
As의 평균함량이 285 mg/kg인 상동광산 광물찌꺼기의 As제거를 위한 부유선별에서 인산염 첨가에 따른 영향을 알아보기 위해 제3인산나트륨(이하 T.S.P)을 분산제로 첨가하여 부유선별을 실시하였다. 먼저 분산제 없이 부유선별을 진행한 결과, As제거율은 88.7%, 부상물의 무게비는 2.52%였고 추가적으로 T.S.P를 첨가하여 부유선별을 실시한 결과 각각 92.74%, 2.26%로 As제거율은 증가하고 부상물의 무게비는 감소하였다. 두 실험의 부상물을 대상으로 입도분석을 진행한 결과, T.S.P를 첨가하지 않은 부상물은 평균입도가 19.34 um, 10 um이하의 양이 전체의 40.2%인 반면 T.S.P를 첨가할 경우, 각각 176.8 um, 6.5%였으며 이를 통해 미립입자의 부유가 억제되었음을 확인하였다. 또한 X.R.F 분석을 통해 두 실험 부상물의 실리카($SiO_2$)함량을 비교해본 결과, T.S.P를 첨가하지 않은 경우 42.74%, 첨가한 부상물의 경우 29.56%로 실리카계열의 친수성입자가 효과적으로 분산되어 부유가 억제되는 결과를 확인하였다.