Electrochemical Characterization of Stainless Steel in Ethanolamine Solution Containing an Alkyl Group using Cyclic Voltammetry

순환전압전류법에 의한 알킬기를 함유한 에탄올아민용액에서 스테인리스의 전기화학적 특성

  • Park, Keun-Ho (Dept. of Chemical Engineering, Changwon National University)
  • 박근호 (창원대학교 화공시스템공학과)
  • Received : 2013.02.06
  • Accepted : 2014.02.28
  • Published : 2014.03.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this work, the current-voltage curves for stainless steel in the ethanolamine solution containing alkyl group were measured using the conventional three electrodes of cyclic voltammetry. Stainless steel as working electrode, Ag/AgCl electrode as reference electrode and Pt wire as counter electrode were used respectively. As a result, the C-V characteristics of stainless steel were to be for an irreversible process due to the oxidation current from cyclic voltammogram, using N-ethylethanolamine and N,N-dimethylethanolamine solutions. Effective diffusivity of corrosion inhibitors was decreased with increasing concentration. It was found from SEM images of the metal that the electrolyte (specific name ?)(0.5 N) as corrosion inhibitor was added into a N, N-diethylethanolamine solution ($1.0{\times}10^{-3}M$) containing copper and nickel, the corrosion inhibiting effect was enhanced.

전형적인 3-전극 시스템의 순환전압전류법을 사용하여 알킬기를 가진 에탄올아민 용액 중에서 스테인리스에 대한 전류-전압 곡선을 측정하였다. 스테인리스는 작업 전극으로, Ag/AgCl 전극은 기준 전극으로, 그리고 백금선은 상대 전극으로 각각 사용하였다. N-에틸에탄올아민과 N,N-디메틸에탄올아민 용액에서의 스테인리스의 C-V특성은 순환전압전류법으로부터 산화전류에 기인한 비가역 공정으로 나타났다. 부식억제제의 확산계수의 효과는 각각 농도 증가에 따라 감소하였다. 금속의 SEM 이미지로부터 0.5 N의 전해질에서 부식억제제인 N,N-디에틸에탄올아민 ($1.0{\times}10^{-3}M$)을 첨가한 경우, 구리와 니켈에서 부식억제 효과가 향상되었다.

Keywords

References

  1. J. H. Kim and D. S. Woo, A Study on the Estimation of Corrosion Characteristics of Corrosion Inhibitor using the Simulated Distribution Loop System, J. KTSWT., 12(4), 67 (2004).
  2. D. S. Woo, S. E. Kuh, B. D. Lee, J. H. Kim, and K. S. Moon, Correlation between Corrosion Rate and Red Water on Application of Corrosion Inhibitor in Drinking Water Distribution System, J. KSWW., 19(1), 68 (2005).
  3. S. E. Kuh, D. S. Woo, D. J. Lee, J. H. Kim, H. W. Ahn, and K. S. Moon, Internal Corrosion Control of Drinking Water Pipes by pH and Alkalinity Control and Corrosion Inhibitor, J. KSWW., 20(4), 215 (2006).
  4. K. E. Kim, B. H. Ryu, S. J. Kim, K. J. Kim, and K. M. Moon, An Electrochemical Study on the Effect of Salt Affecting to Corrosion Behavior of Concrete Reinforced Steel in Natural Sea Water, J. Kor. Soc. Oce. Eng., 14(4), 23 (2000).
  5. J. K. Chon and Y. k. Kim, Inhibition Effect of Amino Acids on the Corrosion of Aluminum in Artificial Sea Water, J. Kor. Electrochem. Soc., 12(4), 311 (2009). https://doi.org/10.5229/JKES.2009.12.4.311
  6. D. S. Woo, B. T. Myung, J. G. Moon, and K. S. Moon, Corrosion Control in the Open Recirculating Cooling System Using Corrosion Inhibitor, J. KSEE., 26(10), 1150 (2004).
  7. Z. Hu, K. Chandran, D. Grasso, and B. F. Smets, Effect of Nickel and Cadmium Speciation on Nitrification Inhibition, Environ. Sci. Technol., 36, 3074 (2002). https://doi.org/10.1021/es015784a
  8. D. S. Won, Y. K. Kim, K. C. Shon, Y. W. Lee, J. H. Choi, and Y. T. Ko, A Study on the characteristics of corrosion inhibitor for stainless steel in LiBr Solution, Proceedings of The SAREK Meetings(summer),971 (2002).
  9. P. G. Cao, J. L. Yao, J. W. Zheng, R. A. Gu, and Z. Q. Tian, Comparative Study of Inhibition Effwcts of Benzotriazole for Metals in Neutral Solutions As Observed with Surface- Enhanced Raman Spectroscopy, Langmuir, 18, 100 (2002). https://doi.org/10.1021/la010575p
  10. G. B. Jung, KR Patent No. 10-2013- 0093293(2013).
  11. A. Yildirim and M. Cetin, Synthesis and evalution of new long alkyl side chain acetamide, isoxazolidine and isoxazoline derivatives as corrosion inhibitors, Corr. Sci., 50, 155 (2008). https://doi.org/10.1016/j.corsci.2007.06.015
  12. K. K. Baek and M. H. Ahn, Evalution of Combined Effect of Organic and Inorganic Inhibitors on The Metals used in Absorption Chiller System, J. Corros. Sci. Soc. Kor., 29(4), 217 (2000).
  13. E. V. Starovoitova, N. N. Andreev, I. A. Gedvillo, A. S. Zhmakina, On the use of surfactants in the production of migrating corrosion inhibitors, Protection of Metals and Physical Chemistry of Surfaces, 45(7), 792 (2009). https://doi.org/10.1134/S2070205109070077
  14. M. Forsyth, A. Phanasgaonkar and B. W. Cherry, Migratory Corrosion Inhibitors for Corrosion Control in Reinforced Concrete, 9th Eur. Symp. on Corrosion Inhibitors, Ferrara: 2000, p. 335.
  15. A. Phanasgaonkar, B. Cherry and M. Forsyth, Organic Corrosion Inhibitors; How do They Inhibit and can They Really Migrate through Concrete?, Australian Maritime Engineering Cooperative Research Centre, Monash University, (1997).
  16. K. H. Park, A Study on the Inhibition Effect of Metal Corrosion Using Organic Copmpound Containing an Amine Group, J. Kor. Oil Chem. Soc., 27(3), 361 (2010).
  17. K. H. Park, Electrochemistry Characterization of Metal Using Monoethanolamine as Corrosion Inhibitor, J. Kor. Oil Chem. Soc., 29(1), 88 (2012).
  18. D. Landolt, "Corrosion and surface Chemistry of metals", p. 204, EPFL Press, Lausanne, Switzerland (2007).
  19. E. E. Stansbury and R. A. Buchman, "Fundamentals of electrochemical corrosion", P. 63, ASM International, Ohio, U.S.A. (2004).
  20. T. C. Son, D. S. Kim, and K. H. Park, Electrochemical Properties of Langmuir-Blodgett (LB) Monolayer Films of Alkyl Bromides Mixture, J. Kor. Oil Chem. Soc., 27(2), 202 (2010).
  21. K. H. Park, Effect of Corrosion Inhibition of Metals Using Organic Compound Containing Amine Group, J. Kor. Oil Chem. Soc., 27(3), 88 (2009).
  22. D. S. Park, Study for Electrode Reaction Characteristics by Cyclic Voltammetry, Poly. Sci. Tec., 14, 356 (2003).
  23. P. T. Kissinger, Laboratory Techniques in Electroanalytical Chemistry, p.86, Marcel Dkker (1984).
  24. K. H. Park, Electrochemistry Characterization of Metal Using Corrosion Inhibitors Containing Amide Functional Group, J. Kor. Oil Chem. Soc., 28(1), 48 (2011).

Cited by

  1. CM440 강에 대한 트리에탄올아민의 부식억제에 관한 연구 vol.32, pp.1, 2014, https://doi.org/10.12925/jkocs.2015.32.1.56