Effect of Acrylic Acid Contents and Inorganic Fillers on Physical Properties of Acrylic Pressure Sensitive Adhesive Tape by UV Curing

아크릴산 함량 및 무기물 충전제가 UV 경화형 아크릴 점착테이프의 물성에 미치는 영향

  • Kim, Dong-Bok (Center for Photofunctional Energy Materials, Dept. of Polymer Science and Engineering, Dankook University)
  • 김동복 (광에너지소재연구센터, 단국대학교 고분자시스템공학과)
  • Received : 2012.10.19
  • Accepted : 2012.11.16
  • Published : 2013.03.25
Download PDF
⟨ Previous Next ⟩

Abstract

Acrylic pressure sensitive adhesive (PSA) tapes were used for the automotive, the electrical and the electronic industries and the display module junction. In this study, the manufacture of high-strength structural tape used 2-ethylhexyl acrylate (2-EHA) and acrylic acid (AAC), and UV irradiation for photo-polymerization, and the semi-structural properties of acrylic PSA tape with the AAC content and inorganic filler $SiO_2$ content were investigated. The initial adhesion strength was lowered by the rigidity of molecule chains due to the use of AAC, and the adhesion strength increased with increasing wetting time. The wetability, contact angle, and SEM images of PSA tapes with various contents of AAC were determined. Without filler, the peel strength and dynamic shear strength of PSA tape showed inverse correlation but the peel strength and dynamic shear strength increased with increasing filler content. From these correlations the PSA tapes could be optimized for the applications requiring high performance.

아크릴 점착테이프는 자동차, 전기전자 및 디스플레이 모듈 접합에 사용된다. 본 연구는 이러한 모듈 접합에 사용되는 고강도 준구조형 점착테이프 제조를 위해 2-ethylhexylacrylate(2-EHA)와 acrylic acid(AAC)를 사용하여 UV 조사에 의한 광중합 및 점착테이프 제조를 위해 광경화를 진행하였고, AAC의 함량 및 무기물 충전제 $SiO_2$ 함량에 따라 아크릴 점착테이프의 물성에 미치는 영향을 고찰하였다. 공단량체로 사용된 AAC의 함량이 많을수록 아크릴고분자 사슬의 강직성이 증가하여 초기 점착력이 낮았고, 시간경과에 따라 점착력이 증가하였으며 테이프의 젖음성, 접촉각 및 SEM 이미지를 통해 확인할 수 있었다. 충전제를 첨가하지 않은 점착테이프의 박리강도와 전단접착강도는 반비례 관계였으나 충전제를 첨가하면 함량 증가에 따라 박리강도 증가와 함께 전단접착강도가 증가하는 비례관계를 보였다. 이러한 상관관계로부터 고강도 준구조형 접착물성을 필요로 하는 용도에 최적화된 아크릴 점착테이프를 제시할 수 있었다.

Keywords

Acknowledgement

Supported by : 경기도지역협력연구센터(GRRC)

References

  1. D. Satas, Handbook of Pressure Sensitive Adhesive Technology, 2nd edition, Van Nostrand Reinhold, New York, 1989.
  2. I. Bened, Pressure-Sensitive Adhesive and Applications, 2nd edition, Marcel Dekker, New York, 2004.
  3. H. J. Choi, I. S. Park, and L. Jang, Korea Patent 100852887 (2008).
  4. I. H. Cho, Korea Patent 1020080109275 (2008).
  5. H. S. Do, S. E. Kim, and H. J. Kim, Preparation and Characterization of UV-Crosslinkable Pressure-Sensitive Adhesives in Adhesion-Current Research and Applications, Wiley-VCH, Weinheim(Germany), 2005.
  6. H. S. Joo, Y. J. Park, H. S. Do, H. J. Kim, S. Y. Song, and K. Y. Choi, J. Adhes. Sci. Technol., 21, 5758 (2007).
  7. H. S. Do, Y. J. Park, and H. J. Kim, J. Adhes. Sci. Technol., 20, 1529 (2006). https://doi.org/10.1163/156856106778666462
  8. Z. Czech and R. Milker, Mater. Sci.-Poland, 23, 1015 (2005).
  9. H. S. Do, S. E. Kim, and H. J. Kim, Adhesion-Current Research and Applications, W. Possart, Editor, Chapter 17, Wiley-VCH, Weinheim (Germany), 2005.
  10. A. Pizzi and K. L. Mittal, Adhesive Technology and Applications, Marcel Dekker, New York, 2003.
  11. A. J. Kinloch, Adhesion and Adhesive: Science and Technology, Chapman and Hall, New York, 1987.
  12. ASTM D 3330-96, Standard Test Method for Peel Adhesion of Pressure Sensitive Tape at $180^{\circ}$ Angle (1997).
  13. J. Feng, C. Lu, L. Zhu, P. Wang, V. Tan, Q. Zhang, S. Teng, S. H. Patel, M. Young, and C. G. Gogos, Adv. Polym. Technol., 26, 272 (2007). https://doi.org/10.1002/adv.20108
  14. P. Hajji, L. David, J. F. Gerard, J. P. Pascault, and G. Vigier, J. Polym. Sci. Part B: Polym. Phys., 37, 3172 (1999). https://doi.org/10.1002/(SICI)1099-0488(19991115)37:22<3172::AID-POLB2>3.0.CO;2-R
  15. L. M. Liu, Z. N. Qi, and X. G. Zhu, J. Appl. Polym. Sci., 71, 1133 (1999). https://doi.org/10.1002/(SICI)1097-4628(19990214)71:7<1133::AID-APP11>3.0.CO;2-N
  16. H. Kaddami, J. F. Gerard, P. Hajji, and J. P. Pascault, J. Appl. Polym. Sci., 73, 2701 (1999). https://doi.org/10.1002/(SICI)1097-4628(19990923)73:13<2701::AID-APP18>3.0.CO;2-F
  17. T. C. Chang, Y. T. Wang, Y. S. Hong, and Y. S. Chiu, J. Polym. Sci. Part A: Polym. Chem., 38, 1772 (2000).
  18. M. C. Park, I. S. Seo, M. C. Lee, H. S. Shin, and J. J. Lim, Polymer(Korea), 23, 625 (1999).
  19. H. C. Son, H. G. Kim, D. H. Lee, and K. E. Min, Polymer(Korea), 32, 313 (2008).
  20. J. W. Park, S. W. Lee, H. J. Kim, D. B. Won, D. B. Kim, K. S. Lee, H. S. Woo, and E. A. Kim, J. Adhesion and Interface, 12, 81 (2011).
  21. P. Tordjeman, E. Papon, and J.-J. Villenave, J. Chem. Phys., 113, 10712 (2000). https://doi.org/10.1063/1.1323956
  22. N. Morel, Ph. Tordjeman, J. Duwattez, and E. Papon, J. Colloid Interf. Sci., 280, 374 (2004). https://doi.org/10.1016/j.jcis.2004.08.010
  23. I. M. Cho, H. G. Kim, D. H. Han, J. C. Lim, and K. E. Min, Polymer(Korea), 34, 226 (2010).
  24. Z. Czech, J. Appl. Polym. Sci., 81, 3212 (2001). https://doi.org/10.1002/app.1775
  25. Z. Czech and R. Milker, J. Appl. Polym. Sci., 87, 182 (2003). https://doi.org/10.1002/app.11303

Cited by

  1. Adhesion Properties on the Molecular Weight and Various Substrates of Multi-layered Structural Acrylic Adhesive vol.39, pp.3, 2015, https://doi.org/10.7317/pk.2015.39.3.514
  2. FTIR을 이용한 아크릴레이트 단량체의 광-열 복합경화 거동 연구 vol.42, pp.4, 2018, https://doi.org/10.7317/pk.2018.42.4.714
  3. 서로 다른 측쇄 종류를 가진 주 단량체에 따른 수성 아크릴계 점착제의 물리적 특성 vol.37, pp.6, 2013, https://doi.org/10.12925/jkocs.2020.37.6.1627