A Study on the Filmic Properties of Polypropylenen by Modification of Hydrogenated Hydrocarbon Resin

수첨석유수지 개질에 의한 폴리프로필렌 필름의 특성 연구

  • Received : 2013.12.09
  • Accepted : 2013.12.20
  • Published : 2013.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, a series of bi-axially oriented films based on homo polypropylene (PP) and hydrocarbon resin (HCR) modified PP were prepared to investigate their mechanical properties, optical properties, permeability to gases and water vapors and shrinkage ratio. Hydrogenated dicyclopentadiene (DCPD) resin and hydrogenated C9 resin were used as HCR in this study. Bi-axially oriented polypropylene (BOPP) films made with PP/HCR blends showed better mechanical properties (higher Young's modulus), better optical properties (lower haze), lower permeability to gases and water vapors and increased shrinkage ratio than BOPP films made with homo-PP. Hydrogenated DCPD resin and hydrogenated C9 resin showed similar contribution to the improvement in mechanical properties and optical properties of BOPP films, but there are a differences in permeability to gases and water vapors and shrinkage ratio.

본 연구에서는 polypropylene (PP)을 기본 고분자로 하여, 석유수지(hydrocarbon resin, HCR) 종류와 함량을 달리하여PP/HCR 블랜드의 열량 거동을 분석하였고, 이를 이용하여 bi-axially oriented polypropylene (BOPP) 필름을 제조한 후 필름의 기계적 물성, 광학적 특성, 가스 및 수증기에 대한 투과도 그리고 수축률을 비교 평가하였다. 이 연구에서 HCR로는 수첨 dicyclopentadiene (DCPD) 수지와 수첨 C9 수지가 사용되었다. Homo-PP 대비 PP/HCR 블랜드는 stiffness의 증가 등 필름의 기계적 물성 증가, 필름의 haze 감소 등의 광학적 특성 향상, 가스 및 수증기에 대한 투과도 감소 그리고 필름의 수축률이 증가되었으며, HCR로 사용된 수첨DCPD수지와 수첨 C9수지는 기계적 물성 및 광학적 물성에서는 유사한 기여도를 보이지만, 가스 및 수증기에 대한 투과도와 필름의 수축률에 있어서는 차이를 보였다.

Keywords

References

  1. S. Cimmino, C. Silvestre, and G. dellaVecchia, J. Appl. Polym. Sci., 92, 3454 (2004). https://doi.org/10.1002/app.20307
  2. S. Cimmino, E. D'Alma, M. L. Di Lorenzo, E. Di Pace, and C. Silvestre, J. Polym. Sci. Part B: Polym. Phys., 37, 867 (1999). https://doi.org/10.1002/(SICI)1099-0488(19990501)37:9<867::AID-POLB1>3.0.CO;2-X
  3. C. Sivestre, S. Cimmino, and M. L. DiLorenzo, J. Appl. Polym. Sci., 71, 1677 (1999). https://doi.org/10.1002/(SICI)1097-4628(19990307)71:10<1677::AID-APP15>3.0.CO;2-K
  4. M. L. Di Lorenzo, S. Cimmino, and C. Silvestre, J. Appl. Polym. Sci., 82, 358 (2001). https://doi.org/10.1002/app.1859
  5. S. Cimmino, R. Greco, M. Iavarone, and C. Sivestre, In preparation.
  6. S. Cimmino, P. Guarrata, E. Martuscelli, C. Silvestre, and P. P. Buzio, Polymer, 32 (1991).
  7. S. Cimmino, E. Di Pace, F. E. Karasz, E. Martuscelli, and C. Silvestre, Polymer, 34 (1993).
  8. E. Caponetti, D. C. Martino, S. Cimmino, M. A. Floriano, E. Martuscelli, C. Silvestre, and R. Triolo, J. Mol. Struct., 383, 75 (1996). https://doi.org/10.1016/S0022-2860(96)09271-X
  9. L. C. Mendes, M. I. B. Tavares, and E. B. Mano, Polym. Test, 15, 53 (1996). https://doi.org/10.1016/0142-9418(95)00027-5
  10. A. Triolo, C. Silvestre, S. Cimmino, E. Martuselli, E. Caponetti, and R. Triolo, Polymer, 39 (1998).
  11. A. Triolo, J. S. Lin, G. D. Wignall, and R. Triolo, Polymer, 41, 3751 (2000). https://doi.org/10.1016/S0032-3861(99)00403-6
  12. J. K. Li, J. Li, S. Chen, S. Zhu, H. Li, Y. Cao, F. Yang, and M. Xiang, J. Appl. Polym. Sci., DOI: 10.1002/APP.38699 (2013).
  13. C. Silvestre, S. Cimmino, and B. Pirozzi, Polymer, 44, 4273 (2003). https://doi.org/10.1016/S0032-3861(03)00393-8
  14. E. E. J. Ewins, D. J. St. Clair, J. R. Erickson, and W. H. Korcz, In The Handbook Pressure-Sensitive Adhesive Technolgy, 2nd ed.; Satas D. Ed., Van Nostrand Reinhold: New York (1989).
  15. DeWitt & Company Incorporated, The Worldwide Hydrocarbon Resin Report, Issue Number 23 (2009).

Cited by

  1. Composite materials based on polyolefins with new petroleum resins pp.00323888, 2018, https://doi.org/10.1002/pen.24849