Abstract
In this study, thermoplastic urethane (TPU) coating yarns were prepared at various extruding temperatures. The fine structure and mechanical properties of resultant TPU coating yarns examined by the wide angle X-ray diffractometer (WAXD), differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMTA), and tensile test. TPU coating yarns (prepared at extruding temperatures at $175^{\circ}C$) were confirmed as a stable fine structure that obtained excellent tensile strength and flexibility. The C samples prepared by optimized conditions made by TPU woven floor mat. The structure of the woven mat is $4{\times}4$ basket weave and have laminated with the EVA foam to obtained final TPU woven floor mat products. The resultant TPU woven floor mat was obtained to 1.5MN of tensile strength, 22% of the elongation, and 0.2MN of tear strength. The weight loss abrasion and the resilience by the ball rebound of the TPU-woven floor mat was prior to those of the PVC subsequently, we were able to develop a woven floor mat with TPU coating yarn and produce an eco-friendly high valuable woven floor mat using an interior product.