Abstract
In this study, physical properties were studied by using latent stretching yarn in order to develop the texturing yarn technique for super bulky yarn, which is better in bulkiness and handle than natural wool and also adds property of synthetic fiber to natural wool. In order to obtain textured conditions by analysing basic properties for manufacturing DTY yarn with super bulky property, DTY 50d/12 after spinning latent yarn spined POY 80d/12 was obtained under the two conditions of (i) false twist(T/M) level 3 in DTY texturing and (ii) draw ratio level 4 in draw texturing. For DTY texturing yarn, Elongation rate increased as the heat treatment time and temperatures increased. In addition, shrinkage became higher as false twist was higher, so that elongation rate became lower. When annealing became longer in time and higher in temperature, initial modulus increased. In addition, as the count of false twist increased, the initial modulus showed higher values. For draw texturing yarn, under the conditions of heat temperature 180 and heating time 30 minutes, shrinkage rate in draw ratio 1.55 and 1.6 draw ratio was 7%, and that in 1.65 and 1.7 draw ratio was 8.5%. High draw ratio samples' tenacity was much influenced by heating time and temperature, but low draw ratio samples' tenacity was influenced not by treated time, but by treated temperature.