Conservation of Seated Iron Śākyamuni Buddha Statue from Goryeo Dynasty

고려(高麗) 철제석가여래좌상(鐵製釋迦如來坐像)의 보존

The National Chuncheon Museum has carried out a conservation process in order to prevent corrosion of the seated iron Śākyamuni Buddha statue from Goreyo Dysnasty for its exhibition. Before the conservation process, the surface of the artifact showed exfoliation and the artifact was damaged from rear to legs so exhibition was impossible. Therefore a process to get rid of pollution and to reinforce and protect the artifact was carried out. Before the reinforcing process, a basic test was carried out using micro crystalline wax type with reference to foreign and domestic experiment results. As a result, as wax(in xylene) 5wt% of Dongnam petrochemical Ltd. showed no efflorescence and little change in surface color and was convenient to use, it was chosen as a reinforcing agent and used to suppress corrosion. For the restoration of damaged parts, an internal support was made and used with an epoxy resin, allowing removable restoration, thus increasing effectiveness for exhibition.

국립춘천박물관은 고려 철제석가여래좌상의 부식방지와 상설전시 활용을 위하여 보존처리를 실시하였다. 처리 전 유물의 상태는 부식으로 인한 표면 박락현상이 관찰되었고 가부좌의 오른편 둔부에서 다리부분까지 결손되어 정상적인 전시가 불가능 하였다. 따라서 표면의 이물질을 제거하고 강화·보호 위한 강화처리 작업이 진행되었다. 강화처리 진행에 앞서 국내·외 연구 자료를 바탕으로 micro crystalline wax계를 선정하여 기초 실험을 실시하였다. 그 결과 (주)동남유화의 wax(in xylene) 5wt%가 백화현상과 표면 색상변화가 적으며 작업에 편리성이 높아 강화제로 선택하여 부식을 억제하였다. 결손부분의 복원은 내부 지지대 제작과 함께 epoxy계 수지를 이용하여 탈착이 가능한 복원을 실시하여 전시 효용성을 높였다.