플라즈마 화학증착법으로 제작한 미세결정질 실리콘 박막 특성에 관한 연구

A Study on Characteristics of Microcrystalline-silicon Films Fabricated by PECVD Method

  • 이호년 (순천향대학교 전자정보공학과) ;
  • 이종하 (순천향대학교 전자정보공학과) ;
  • 이병욱 (순천향대학교 전자정보공학과) ;
  • 김창교 (순천향대학교 전자정보공학과)
  • 발행 : 2008.09.01

초록

Characteristics of microcrystalline-silicon thin-films deposited by plasma-enhanced chemical-vapor deposition (PECVD) method were studied. There were optimum values of RF power density and $H_2$ dilution ratio $(H_2/(SiH_4+H_2))$; maximum grain size of about 35 nm was obtained at substrate temperature of 250 $^{\circ}C$ with RF power density of 1.1 W/$cm^2$ and $H_2$ dilution ratio of 0.91. Larger grain was obtained with higher substrate temperature up to 350 $^{\circ}C$. Grain size dependence on RF power density and $H_2$ dilution ratio could be explained by etching effects of hydrogen ions and changes of species of reactive precursors on growing surface. Surface-mobility activation of reactive precursors by temperature could be a reason of grain-size dependence on the substrate temperature. Microcrystalline-silicon thin-films that could be used for flat-panel electronics such as active-matrix organic-light-emitting-diodes are expected to be fabricated successfully using these results.

키워드

참고문헌

  1. H. Miyashita and Y. Watabe, "Dependence of thin film transistor characteristics on the deposition conditions of silicon nitride and amorphous silicon", IEEE Transactions on Electron Devices, Vol. 41, No. 4, p. 499, 1994 https://doi.org/10.1109/16.278501
  2. T. Sameshima, "Status of Si thin film transistors", Journal of Non-Crystalline Solids, Vol. 227-230, p. 1196, 1998 https://doi.org/10.1016/S0022-3093(98)00299-3
  3. K. Kandoussi, A. Gaillard, C. Simon, N. Coulon, T. Pier, and T. Mohammed-Brahim, "Improved microcrystalline silicon TFTs", Journal of Non-Crystalline Solids, Vol. 353, p. 1728, 2006
  4. S. Ferrero, P. Mandracci, G. Cicero, F. Giorgis, C. F. Pirri, and G. Barucca, "Large area microcrystalline silicon films grown by ECR-CVD", Thin Solid Films, Vol. 383, p. 181, 2001 https://doi.org/10.1016/S0040-6090(00)01630-8
  5. T. Karakawa, S. Higashi, H. Murakami, and S. Miyazaki, "Nucleation study of hydrogenated microcrystalline silicon (${\mu}$ c-Si:H) films deposited by VHF-ICP", Thin Solid Films, Vol. 56, p. 3497, 2008
  6. A. Matsuda, "Formation kinetics and control of microcrystallite in ${\mu}$c-Si:H from glow discharge plasma", Journal of Non- Crystalline Solids, Vol. 59 & 60, p. 767, 1983