Abstract
Structural and magnetic properties of $CO_{1-x}Zn_xZ$ ($Ba_3Co_{1-x}Zn_xFe_{24}O_{41}$) hexa-ferrite are studied using XRD, VSM and SEM, respectively. Powder was prepared from co-precipitation and firstly heat treated at $1350^{\circ}C$ for 6 hours in $O_2$ atmosphere. Second heat treatment was performed at 900, 1000, $1100^{\circ}C$ for 6 hours in air, respectively. Saturation magnetization value of first heat treated powder is acceptable and coercivity is high for applying to device. These result may be originated from incomplete formation reaction from M and Y phases to Z phase. Second heat treatment leads to small value of coercivity.