Synthesis of Nano-Colloidal Silica Coated with Silver

은을 코팅한 Nano-Colloidal Silica의 합성

  • Lee, Joo-Heon (Department of Environmental Engineering, Daegu University) ;
  • Lim, Yoon-Hee (Department of Environmental Engineering, Daegu University) ;
  • Ham, Jae-Yong (Department of Chemical Engineering, Daegu University)
  • 이주헌 (대구대학교 환경공학과) ;
  • 임윤희 (대구대학교 환경공학과) ;
  • 함재용 (대구대학교 화학공학과)
  • Received : 2007.08.27
  • Accepted : 2007.12.12
  • Published : 2008.02.10
Download PDF
⟨ Previous Next ⟩

Abstract

The self assembled silver process and silver coating process after surface reforming for silica particle, were investigated to coat the silver to colloidal silica. The effects of silver amounts and reductant amounts on silver coating efficiencies were investigated. The silver coating process after surface reforming for silica particle using MPTS (3-Mercaptopropyl trimethoxysilane) and APTS (3-Aminopropyl trimethoxysilane), showed the higher coating efficiency and better antibacterial effect than the self assembled silver process.

본 연구에서는 나노 콜로이드 실리카에 은을 코팅하기 위하여 직접 은을 코팅하는 방법과 실리카입자 표면개질 후 은을 코팅하는 방법 등의 2가지 방법이 시도되었다. 실리카에 대한 은의 질량비율과 환원제 주입량 등이 은의 코팅에 미치는 영향을 조사하였다. 콜로이드 실리카에 직접 은을 코팅한 경우보다 MPTS (3-Mercaptopropyl trimethoxysilane)와 APTS (3-Aminopropyl trimethoxysilane)로 표면개질한 후 은을 코팅한 경우가 높은 은(Ag) 코팅율과 우수한 항균효과를 나타내는 것이 관찰되었다.

Keywords

Acknowledgement

Supported by : 대구대학교

References

  1. K. H. Kim, I. H. Lee, H. S. Lee, and J. K. Park, Prospectives of Ind. Chem., 6, 46 (2003)
  2. K. H. Cho and S. G. Park, J. Korean Ind. Eng. Chem., 15, 952 (2004)
  3. R. Patakfalvi and I. Dekany, Appl. Clay Sci., 25, 149 (2004) https://doi.org/10.1016/j.clay.2003.08.007
  4. W. X. Zhang, J. Nanoparticle Research, 5, 323 (2003) https://doi.org/10.1023/A:1025520116015
  5. S. L. Westcott, S. J. Oldenburg, T. R. Lee, and N. J. Halas, Langmuir, 14, 5396 (1998) https://doi.org/10.1021/la980380q
  6. L. M. Liz-Marzan, M. Giersig, and P. Mulvaney, Langmuir, 12, 4329 (1996) https://doi.org/10.1021/la9601871
  7. R. D. Badley, W. T. Ford, F. J. McEnroe, and R. A. Assink, Langmuir, 6, 792 (1990) https://doi.org/10.1021/la00094a013
  8. D. B. Zhang, H. M. Cheng, and J. M. Ma, J. Materials Sci. Letters, 20, 439 (2001) https://doi.org/10.1023/A:1010906615079
  9. F. Porta, L. Prati, M. Rossi, S. Coluccia, and G. Martra, Catal. Today, 61, 165 (2000) https://doi.org/10.1016/S0920-5861(00)00370-9
  10. Y. Zhu, Y. Qian, M. Zhang, and Z. Chen, Materials Letters, 17, 314 (1993) https://doi.org/10.1016/0167-577X(93)90021-O
  11. Y. H. Kim, J. Korean Ind. Eng. Chem., 14, 487 (2003)