Electrical Properties of BaTiO3 Thick Films Fabricated by Screen-printing Method

  • Ahn, Byeong-Lib (Department of Electrical Engineering, Hanyang University) ;
  • Lee, Sung-Gap (Department of Ceramic Engineering, Eng. Res. Insti., Gyeongsang National University)
  • Published : 2007.08.31

Abstract

[ $(Ba_{0.6}Sr_{0.3}Ca_{0.1})TiO_3$ ](BSCT) thick films doped with 0.1 mol% $MnCO_3\;and\;Yb_2O_3(0.1{\sim}0.7mol%)$ were fabricated by the screen printing method on the alumina substrates. And the structural and electrical properties as a function of $Yb_2O_3$ amount were investigated. The exothermic peak was observed at around $680^{\circ}C$ due to the formation of the poly crystalline perovskite phase. The lattice constants of the BSCT thick film doped with 0.7 mol% is 0.3994 nm. The specimen doped with 0.7 mol% $Yb_2O_3$ showed dense and uniform grains with diameters of about $4.2{\mu}m$. The average thickness of all BSCT thick films was approximately $70{\mu}m$. Relative dielectric constant and dielectric loss of the specimen doped with 0.7 mol% $Yb_2O_3$ were 2823 and 3.4%, respectively. The Curie temperature of the BSCT thick films doped with 0.1 mol% $Yb_2O_3$ was $46^{\circ}C$.

Keywords

References

  1. S. G. Lee and S. H. Lee, 'Dielectric properties of Zrdoped (Ba,Sr,Ca)$TiO_3$ thick films for microwave phase shifters', Trans. EEM, Vol. 4, No.2, p. 24, 2003
  2. S. G. Lee, Y. H. Lee, and S. G. Bae, 'A study on the structural and dielectric properties of (Ba,Sr,Ca)$TiO_3$ thick films with sintering conditions', J. of KIEEME (in Korean), Vol. 14, No.6, p. 460, 2001
  3. B. Jaffe, W. R. Cook, and H. Jaffe, 'Piezoelectric Ceramics', Academic Press, New York, p. 94, 1971
  4. T. Hayashi, H. Shinozaki, and K. Sasaki, 'Preparation of $(Ba_{x}Sr_{1-x})TiO_3$ particle by vaporphase hydrolysis of precursors formed from alkoxide-hydroxide', Jap. J. Appl. Phys., Vol. 37, p. 5232, 1998
  5. B. Jaffe, W. R. Cook, and H. Jaffe, 'Piezoelectric Ceramics', Academic Press, New York, p. 238,1971
  6. F. D. Morrison, D. C. Sinclair, and A. R. West, 'Doping mechanism and electrical properties of Ladoped $BaTiO_3$ ceramics', Int. J. Inorganic Materials, Vol. 3, p. 1205,2001
  7. R. C. Buchanan, 'Ceramic Materials for Electronics', Dekker, New York, pA7, 1986