Silsesquioxane/Polystyrene Hybrid Materials via Charge Transfer Interactions

전하 이동을 이용한 실세스퀴옥산/폴리스티렌 하이브리드

  • Choi, Ji-Won (Department of Chemical Engineering, Kyung Hee University) ;
  • Chujo, Yoshiki (Department of Polymer Chemistry, School of Engineering, Kyoto University)
  • 최지원 (경희대학교 환경응용화학대학 화학공학.영상정보소재기술연구센터) ;
  • 요시키 주조 (교토대학교 고분자화학과 일본)
  • Published : 2007.03.31
Download PDF
⟨ Previous Next ⟩

Abstract

Charge transfer interaction as a hybridization mechanism of silsesquioxane/polymer was tested using carbazole (electron donor) group and dinitrobenzene (electron acceptor) group. Hybridization test was conducted using films made from mixing/casting of poly (carbazole-styrene) (PS/D) and dimtrobenzyl silsesquioxane (Cube/A), and transparent hybrid films were successfully obtained under some conditions. $^1H-NMR$ of PS/D and Cube/A, and W absorption test of hybrid films showed that one acceptor and one donor can form one charge transfer complex when no silsesquioxane molecule was included in films, but transparent hybrids with no phase separation were obtained only at acceptor/donor ratios less than 0.7 : 1. These results also suggested that on average 4 charge transfer complexes form per one silsesquioxane.

Carbazole(electron donor)그룹과 dinitrobenzene(electron acceptor)그룹을 이용하여 전하 이동 작용이 실세스퀴옥산/고분자 하이브리드의 형성 메커니즘으로서 작용할 수 있는지 살펴보는 연구를 진행하였다. 하이브리드 실험은 새롭게 합성된 Poly(carbazole-styrene) (PS/D)와 dinitrobenzyl silsesquioxane (Cube/A)의 톨루엔 용액을 혼합/캐스팅을 하여 만들어진 필름을 이용하였으며 상분리가 없는 투명한 하이브리드 필름이 일부 조건에서 얻어졌다. PS/D및 Cube/A의 $^1H-NMR$분석, 그리고 하이브리드 필름들의 UV 흡수 실험은 실세스퀴옥산에 의한 입체 장애 효과가 없는 조건에서는 acceptor와 donor가 1:1로 전하 이동 착물을 형성할 수 있지만, 상분리가 없는 투명한 실세스퀴옥산 하이브리드는 acceptor/donor의 비율이 0.7 : 1 이하에서 형성된다는 것을 보여주었다. 이 결과들은 또 실세스퀴옥산 한 분자 당 평균 4개의 전하 이동 착물이 형성된다는 하이브리드 나노 구조에 대한 정보도 제공하였다.

Keywords

References

  1. S. J. Wang, C. F. Long, X. Y. Wang, Q. Li, and Z. N. Qi, J. Appl. Polym. Sci., 69, 1557 (1998)
  2. P. B. Messersmith and E. P. Giannelis, J. Polym. Sci.; Part A : Polym. Chem., 37, 2225 (1999)
  3. J. G. Doh and I. Cho, Polym. Bull., 41, 511 (1998)
  4. B. Abramoff and J. Covino, J. Appl. Polym. Sci., 46, 1785 (1992)
  5. P. C. Pebaron, Z. Wang, and T. Pinnavaia, J. Appl. Clay Sci., 15, 11 (1999)
  6. C. G. Reid and A. R. Greenberg, J. Appl. Polym. Sci., 39, 9951 (1990)
  7. T. T. Che, R. V. Carney, G. Khananarian, R. A. Keosiuan, and M. Bozo, J. Non -Cryst. Solids, 102, 280 (1988)
  8. P. H. Sung and C. Y. Lin, Eur. Polym., 33, 903 (1997) https://doi.org/10.1016/S0014-3057(96)00303-5
  9. D. A. Loy and K. J. Shea, Chem. Rev., 95, 1431 (1995)
  10. B. M. Novak, Adv. Mater., 5, 422 (1993)
  11. R. M. Laine, J. Choi, and I. Lee, Adv. Mster., 13, 800 (2001)
  12. J. Choi, R. Tamaki, S. G. Kim, and R. M. Laine, Chem. Mater., 15, 3365 (2003) https://doi.org/10.1021/cm030286h
  13. J. Choi, S. G. Kim, and R. M. Laine, Macromolecules, 37, 99 (2004) https://doi.org/10.1021/ma030309d
  14. M. C. Castex, C. Olivero. G. Pichler, D. Ades, E. Cloutet, and A. Siove, Synthetic Met., 122, 59 (2001) https://doi.org/10.1016/S0379-6779(00)01318-7
  15. T. Yasuda, T. Imase, and T. Yamamoto, Macromolecules, 38, 7378 (2005) https://doi.org/10.1021/ma051102i
  16. K. R. J. Thomas, J. T. Lin, Y.-T. Tao, and C.-H. Chuen, Chem. Mater., 16, 5437 (2004) https://doi.org/10.1021/cm048794u
  17. S. A. Jenekhe, L. Lu, and M. M. Alam, Macromolecules, 34, 7315 (2001) https://doi.org/10.1021/ma002404h
  18. J. M. G. Cowie and A. Demaude, Polym. Adv. Tech., 5, 178 (1994)
  19. H. A. Schneider, H. J. Cantow, and V. Percec, Polym. Bull., 6, 617 (1982)
  20. H. A. Schneider, U. Epple, B. Leikauf, and H. A. Neto, New Polym. Mater., 3, 115 (1992)
  21. X. Li, B. Wu, J. Huang, J. Zhang, Z. Liu, and H. Li, Carbon, 411, 1645 (2002)
  22. L. Valentini, I. Armentano, L. M. Kenny, S. Bidali, and A. Mariani, Thin Solid FIlms, 476, 162 (2005) https://doi.org/10.1016/j.tsf.2004.09.051
  23. M. Pientka, V. Dyakonov, D. Meissner, A. Rogach, D. Talapin, H. Weller, L. Lutsen, and D. Vanderzande, Nanotechnology, 15, 163 (2004) https://doi.org/10.1088/0957-4484/15/1/032
  24. N. Ballav, Mater. Lett., 59, 3419 (2005) https://doi.org/10.1016/j.matlet.2005.05.078
  25. Y. Shimazaki, M. Mitsuishi, S. Ito, and M. Yamamoto, Langmuir, 14, 2768 (1998)
  26. Y. Shimazaki and S. Ito, Langmuir, 16, 9478 (2000)
  27. Y. Shimazaki, M. Mitsuishi, S. Ito, and M. Yamamoto, Langmuir, 13, 1385 (1997)
  28. S. Setz and H. A. Schneider, Makromol. Chem., 194, 233 (1993) https://doi.org/10.1002/macp.1993.021940322
  29. M. Bolsinger and H. A. Schneider, Makromol. Chem., 195, 2683 (1994)
  30. A. Simmons and A. Natansohn, Macromolecules, 23, 5127 (1990)
  31. A. Simmons and A. Natansohn, Macromolecules, 24, 3651 (1991)
  32. G. Odian, Principles of Polymerization, Wiley Interscience, New York, p.456 (1991)