Abstract
As a basic study on the conversion of molten converter slag to the ordinary portland cement, the effects of $Al_{2}O_{3}$ addition on the interface reaction between solid CaO and molten converter slag has been studied. Alumina added converter slag whose basicity was controlled to 1 and 2 was melted and hold for 30 minutes in MgO crucible at $1500^{\circ}C$. Then sintered CaO pellet heated at the same temperature was dipped into the molten slag and held for 30minutes. After the reaction, the crucible was cooled in air and the specimen was cut off to the horizontal direction of the crucible. The dissolution rate of CaO pellet with the addition of $Al_{2}O_{3}$ was measured by the change of the radius or sintered CaO pellet and the interface layer was observed by SEM/EDX. As a result. At the basicity 2 slag, thickness of created $C_{3}S$ layer increased 3.5 times and quantity of $C_{6}AF_{2}\;or\;C_{4}AF$ phase increase 2 times than baisicy 1 slag.
용융전로슬래그로부터 일반 포틀랜드 시멘트로의 전환에 관한 기초 연구의 일환으로, 전로슬래그의 $Al_{2}O_{3}$ 농도에 따를 고체 CaO 입자와 용융슬래그간의 계면반응을 알아보고자 하였다. 염기도($B=CaO/SiO_2$)를 1과 2로 조정한 전로슬래그에 소정의 $SiO_2$와 $5{\sim}15wt%\;Al_{2}O_{3}$를 첨가제로 첨가하여 MgO도가니에 넣고 $1500^{\circ}C$에서 30분간 가열 용해하여 균질화 한 후, 같은 온도의 소결 CaO펠렛을 투입하여 $10{\sim}30$분간 반응시켰다. 반응 후 급냉한 시편을 도가니의 직경방항으로 절단해서 펠렛 단면의 CaO직경 변화를 측정하여 슬래그중 $Al_{2}O_{3}$첨가에 따른 CaO의 용해속도를 조사하고, 계면 생성층을 SEM/EDX로 관찰하였다. 그 결과, 슬래그의 염기도가 2인 경우, 염기도가 1인 경우 보다 생성층 $C_{3}S$상의 두께는 $Al_{2}O_{3}$를 15wt.%까지 첨가함에 따라 3.5배 증가하였으며, $C_{6}AF_{2}$ 또는 $C_{4}AF$양도 2배 정도 증가됨을 알 수 있었다.