A Study of Adhesion Process on the Footwear Cotton Fabric Treated with Sericite Antibacterial Agent

Sericite 항균처리 신발용 면직물의 접착공정 연구

  • Yoon, Rae Won (Ilshintextile) ;
  • Lee, Jae Ho (Department of Biomaterial Engineering, Pusan National University) ;
  • Cho, Hyun Hok (Department of Textile Engineering, Pusan National University)
  • Received : 2006.05.11
  • Accepted : 2006.05.29
  • Published : 2006.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, we used a sericite which is a cheap price antibacterial agent and had excellent results. The particle size of sericite was fixed to $15{\mu}m$. The effect of the peel strength is not affected by several types of adhesives. Peel strength is increased with increasing adhesive content, and satisfied standard value of peel strength when adhesive content is $20g/m^2$. Laundering cotton fabric treated with antibacterial agent, the optimum content satisfying Korean Standard (KS) is 8%. Continuous processing conditions for antibacterial treatment on the footwear cotton fabrics are follows : melting temperature $120^{\circ}C$, cooling time 20 s, pressing temperature $130^{\circ}C$, pressing time 30 s.

본 연구에서는 가격이 저렴하고 우수한 결과를 갖는 항균제인 견운모(sericite)를 사용하였다. 견운모의 입자 크기는 $15{\mu}m$로 고정하였다. 박리강도의 효과는 접착제의 종류에 영향을 받지 않았다. 박리강도는 접착제 함량이 증가함에 따라 증가하였고, 접착제 함량이 $20g/m^2$ 일 때 기준 값을 만족하였다. 항균제로 처리된 면직물의 한국공업규격(KS) 세탁견뢰도를 만족하는 항균제 함량은 8%이다. 신발용 면직물에 있어 항균처리를 위한 연속적인 공정 조건들은 다음과 같다: 용융온도 $120^{\circ}C$, 냉각시간 20 s, 압착온도 $130^{\circ}C$, 압착시간 30 s.