Abstract
[ $Pb(Zr_{0.2}Ti_{0.8})O_3/SrRuO_3$ ] heteroepitaxial thin films were deposited at various temperatures on single crystal $SrTiO_3$ substrates by pulsed laser deposition and characterized for the microstructural and ferroelectric properties. The $SrTiO_3$ substartes etched by buffered oxide etch $(pH{\thickapprox}5.8)$ solution for 20s followed by the thermal annealing at $1000^{\circ}C$ for 1h showed the terrace ledges with a 0.4nm height. The $SrRuO_3$ bottom electrodes with a thickness of 52nm grown on $SrTiO_3$ single crystal also exhibit a terrace ledge similar to that of $SrTiO_3$. The PZT thin films were grown with an epitaxial relationship and showed typical P-E hysteresis loops shown at the epitaxial films. The 56nm thick-PZT films deposited at $650^{\circ}C$ exhibit a remanent polarization $(p_r)$ of $80{\mu}C/cm^2$ and a coercive field $(E_c)$ of 160kV/cm.