The Removal of Heavy Metals from Treeated Wood by Biological Methods (II) - Removal of Heavy metals from CCA and CCFZ- treated Wood -

생물학적인 방법을 이용한 방부처리재의 중금속 제거 (II) - CCA, CCFZ 처리재에서 중금속 제거 -

Heavy metals were removed from CCA- and CCFZ- treated wood using a brown-rot fungi Tyromyces palustris. The amount of effective elements extracted from treated woods was compared for different treatment methods. The relationship between the amount of heavy metals removed and concentrations of oxalic acid for treated wood was examined. Also, the relationship between mycelia weight and removal rate was examined. The removed quantity of heavy metal from treated wood according to fermentation methods was examined. The extraction amount of chromium and arsenic components increased with increasing oxalic acid concentration, but the extraction amount of copper did not improved much. A 287 mg of mycelia weight can remove chromium and arsenic over 60% in 3 g CCA chips and copper was also removed over 50%. The chromium, copper and arsenic were removed over 60% by shaking fermentation, the removal rate of copper by static cultivation was higher than that of shaking fermentation. The removal rate of chromium, copper and arsenic were 72%, 61% and 59% with air-lift bioreactor, respectively.

갈색부후균 Tyromyces palustris를 이용하여 CCA처리 목재와 CCFZ처리 목재에서 중금속을 제거하였다. 전처리 방법으로써 증기압처리와 수산처리가 검토되었다. 수산 전처리에 의한 균처리의 제거율 상승 영향과 일정 균체량에 대한 방부처리재의 폭로양의 차이에 따른 처리율의 변화정도를 검토하였다. 배양방법을 달리하여 방부처리재의 유효성분 제거량을 비교하고 생물반응기를 이용하여 중금속 제거를 실시하였다. 크롬과 비소는 수산의 농도가 증가할수록 제거율이 증가하였으나 구리는 농도의 증가에 따른 제거율이 크게 향상되지 않았다. T. palustris는 균체량 287 mg으로 크롬과 비소는 시료무게 3 g까지 60% 이상의 제거율을 나타냈고 구리는 50% 이상의 제거율을 나타내었다. 진탕배양에서는 크롬, 구리, 비소의 제거율이 60% 이상의 제거율을 보였으며, 정치배양에서는 구리의 제거율이 진탕배양보다 높게 나타났다. 생물반응기 적용 시 7일 배양이후 제거율은 크롬 72%, 구리 61%, 비소는 59%이었다.