A Study on Dynamic Properties of Short-fiber Reinforced Chloroprene Rubber

단섬유 강화 Chloroprene 고무의 동적특성 연구

The dynamic properties of short-fiber reinforced chloroprene rubber with different interphase conditions and fiber contents have been studied as functions of frequency, amplitude and temperature. The loss factor(LF) slightly increased more than 1.33% of strain and the dynamic ratio(DR) rapidly decreased with increasing strain amplitude. The LF rapidly decreased with increasing frequency especially more than 50Hz. The DR showed the lower when it compared to virgin material with increasing frequency. The LF showed the maximum at $65^{\circ}$ and rapidly decreased after that temperature. The DR showed the lower when it compared with virgin rubber with increasing temperature. Generally, the better interphase condition showed the lower LF and DR at the same testing condition. Therefore, the short-fiber reinforced rubber could have the better isolation when the frequency ratio is more than $\sqrt{2}$ compared with frequency ratio less than $\sqrt{2}$.

계면상 조건과 섬유 함유량 변화에 따른 단섬유 강화 CR의 동적특성에 대해 주파수, 진폭 그리고 온도를 함수로 실험적 고찰을 하였다. 진폭 변형률 증가에 따라 LF는 1.33% 이상에서 약간 증가하였고, DR은 크게 감소하였다. 주파수 증가에 따라 LF는 특히 50Hz 이후 크게 감소하였고, DR은 기지고무보다 낮은 값을 보였다. 온도 증가에 따라 LF는 $65^{\circ}$에서 최대 값을 나타내고 이후 크게 감소세를 보였다. DR은 온도가 증가에 따라 기지고무 보다 낮은 값을 보였다. 일반적으로 동일한 시험 조건에서 계면상이 우수할수록 LF와 DR이 낮은 값을 보였다. 따라서 단섬유 강화고무는 진동 수비가 $\sqrt{2}$ 이하보다는 $\sqrt{2}$ 이상에서 더 큰 진동절연 효과가 있다고 할 수 있다.