Physical Properties of Fabric E-Glass Fiber Reinforced Laminated Timber (II) - Peeling and vapor adsorption properties -

직물유리섬유강화 집성재의 물리적 특성(제2보) - 박리 및 흡습성 -

  • Jung, In-Suk (Department Group of Forestry and Wood Science & Technology, Kyungpook National Univ.) ;
  • Lee, Weon-Hee (Department Group of Forestry and Wood Science & Technology, Kyungpook National Univ.) ;
  • Kim, Jong-Man (College of Agriculture, Gyeongsang National University)
  • 정인석 (경북대학교 임학․임산공학과) ;
  • 이원희 (경북대학교 임학․임산공학과) ;
  • 김종만 (경상대학교 농과대학)
  • Received : 2002.09.13
  • Accepted : 2002.12.26
  • Published : 2003.10.26
Download PDF
⟨ Previous Next ⟩

Abstract

This study was conducted to estimate peeling and vapor adsorption properties made with fabric glass fiber reinforced laminated timber according to our earlier report(Jung et al., 2002). In adsorption peeling test, three all types solid wood were not appeared the peeling. However, solid wood appeared to the peeling in boiling peeling test except for control wood. Vapor adsorption test was performed at 40℃, 90% relative humidity for 48 hours. Cross sections were not different all solid wood. Radial section and tangential section with glass fiber were delayed vapor adsorption compared to control wood. In anisotropy of vapor adsorption, solid wood with glass fiber were small values.

본 연구는 전보(정 등, 2002)에서 제조된 직물유리섬유 강화집성재의 박리 및 수분 흡착특성을 조사해 보기 위해서 실시되었다. 침지 박리시험에서, 3가지 형태의 소재 모두 박리를 나타내지 않았지만, control재를 제외한 모든 형태의 소재는 삶음 박리에서 박리가 발생하였다. 수분흡착시험은 40℃, 상대습도 90% 조건에서 48시간동안 실시하였다. 횡단면 흡습성은 모든 소재에서 다르지 않았다. 유리섬유로 된 소재에서 방사단면과 접선단면은 control재와 비교하여 수분 흡착이 지연되었다. 수분흡착 이방성에서, 유리섬유 함입된 소재는 적은 수분흡착을 나타내었다.