Abstract
The purpose of this study is to clarify the effect of the monomer ratio on properties of the polymer-modified mortars using methylmethacrylate-butyl acrylate(MMA/BA) latexes, and to obtain basic data necessary to develop appropriate latexes for cement modifiers. From the test results, we knew that the pore volume of polymer-modified mortars using MMA/BA latexes at bound MMA contents of 60 and 70 percent is 7.5∼75nm and the fine pore volume is increased with an increase in the polymer-cement ratio. The total pore volume of polymer-modified mortars using MMA/BA latexes is linearly reduced with an increase in the bound MMA content and increased in the polymer-cement ratio. In general, the superior compressive strength of polymer-modified mortars using MMA/BA latexes is obtained at a bound MMA content of 70 percent and a polymer-cement ratio of 15%. And, the water absorption and chloride ion penetration depth are greatly affected by the polymer-cement ratio rather than the bound MMA content. The important factors affecting the properties of polymer-modified mortars using MMA/BA latexes polymerized with various monomer ratios are the variations of the pore size distribution with changing bound MMA content and the polymer-cement ratio.
본 연구에서는 MMA/BA 합성 라텍스를 이용하여 폴리머 시멘트 모르타르의 성질에 영향을 미치는 모노머비의 효과를 검토하고, 시멘트 혼화용 폴리머로서의 개발적용을 위해 필요한 기초적 실험 데이터를 얻기 위한 것이다. 실험결과, MMA/BA모노 머비에 따른 폴리머 시멘트 모르타르의 세공경 분포는 MMA/BA의 비가 60 : 40, 70 : 30에서 미세공극량이 크게 증가했으며, 전세공용적은 감소하였다. 또한 모노머비에 관계없이 폴리머 시멘트 비가 증가할수록 그 효과는 더욱 커지는 것으로 나타났다. 일반적으로 MMA/BA 혼입 폴리머 시멘트 모르타르의 압축강도는 MMA 결합재량 70% 및 폴리머-시멘트비 15%에서 가장 우수하게 나타났으며, 흡수율과 염화물 이온 침투저항성은 MMA 결합재량보다는 폴리머-시멘트비에 의해 크게 지배되는 것으로 나타났다. 모노머비를 변화한 MMA/BA 합성 라텍스 혼입 폴리머 시멘트 모르타르의 성질에 영향을 미치는 중요한 인자는 MMA 결합재량의 변화에 의한 세공경분포의 변화와 폴리머-시멘트비로 나타났다.