A STUDY ON THE MICROSCOPIC IMAGES OF DENTIN SURFACES IN PRIMARY TEETH ACCORDING TO SURFACE WETNESS AFTER ACID ETCHING

유치 상아질 산부식 후 습윤 정도에 따른 조직상

  • Oh, Young-Jun (Department of Pediatric Dentistry, College of Dentistry, Pusan National University) ;
  • Jung, Tae-Sung (Department of Pediatric Dentistry, College of Dentistry, Pusan National University) ;
  • Kim, Shin (Department of Pediatric Dentistry, College of Dentistry, Pusan National University)
  • 오영준 (부산대학교 치과대학 소아치과학교실) ;
  • 정태성 (부산대학교 치과대학 소아치과학교실) ;
  • 김신 (부산대학교 치과대학 소아치과학교실)
  • Published : 2003.11.29

Abstract

To achieve good dentin bonding, we must obtain proper wet dentin surface. The purpose of this study was to compare dentin surface according to different wetness degree by AFM image as studying how to obtaining proper wet dentin surface. Intact recently extracted primary teeth were used in the study. The extracted teeth were stored in distilled water at $4^{\circ}C$ until prepared. The teeth were used to prepare 1mm thick dentin disks with exposed surfaces parallel to the occlusal surfaces. The surface of the dentin were polished with polishing disk. The sample were ultrasonically cleaned with distilled water. The sample of each group were treated by different ways. We compared dentin surface of each group by AFM image. From the experiment, the following results were obtained. 1. Acid etching in the dentin surface of primary teeth, resulted in the removal of the smear layer, which opened dentinal tubules, caused the demineralization of peritubular and intertubular dentin, and exposed a collagen-rich transition zone. 2. If the etched dentin was so dehydrated, the intertubular dentin surfaces deceased in height and the diameters of the dentinal tubules decreased slightly. 3. In the group dried with compressed air for 20 seconds at 2 cm, the dentin surfaces were too excessive dried and dehydrated. 4. In the group dried with compressed air for 3 seconds at 2 cm, dry cotton, wet cotton, microbrush and absorbent tissue paper, the dentin surfaces were properly wet.

상아질 접착력을 높이기 위해서는 적절히 습윤한 상아질 표면을 얻는 것이 중요하다. 이런 방법에는 정확한 지침이 없으며, 주관적이고 술자에 따라 많은 차이가 있다. 본 연구에서는 적절히 습윤한 상아질을 얻는 방법에 관한 연구의 일환으로, 유치의 산부식 후. 여러 가지 방법을 이용해 상아질을 건조시킨 표본의 조직상을 획득하여 상아질 표면의 차이를 비교하고자 하여 다음과 같은 결론을 얻었다. 1. 유치 상아질을 산부식하면, 도말층이 제거되고 상아세관이 노출되며, 관간상아질과 관주상아질이 탈회되고, 교원섬유가 풍부한 이행층이 노출되는 것을 확인할 수 있었다. 2. 산부식된 상아질이 과도하게 건조되면 탈회된 상아질이 수축하여, 관간상아질이 붕괴되어 높이가 점차적으로 낮아지고 상아세관의 직경은 조금씩 감소되는 것으로 나타났다. 3. 유치 산부식 후, 10cm 거리에서 20초 동안 압축 공기로 건조시키면 상아질이 과도하게 건조, 탈수됨을 확인할 수 있었다. 4. 유치 산부식 후, 10cm 거리에서 3초 동안 압축 공기로 건조시키거나 마른 cotton, 젖은 cotton, microbrush, absorbent tissue paper로 건조시키면 상아질이 적절하게 건조됨을 확인할 수 있었다.