Abstract
Mineral medicines are single or mixtures of minerals and rocks which have been used to treat disease. Recently, their application has been increased by emphasizing the physical properies of the medicines, in addition to their chemical properies. In this study, mineralogical, chemical, spectroscopic and magnetic properties were measured using X-ray diffraction analysis, X-ray fluorescence spectrometry, Ff-Infrared spectroscopy, nuclear magnetic resonance spectroscopy, mass magnetic susceptibility. Experiments were done using these properties to evaluate application of traditional mineral medicines such as Yanggiseok, Yeonok and Eumgiseok. Mineralogical study proves that Yanggiseok, generally known as tremolite, consists of actinolite. Yeonok for medical usage mostly consists of fine grained tremolite. Eumgiseok is mainly composed of vermiculite and minor kaolinite and halloysite. Yeonok and Yanggiseok, belong to the amphibole group among inosilicates and both have similar emission power properties. The intensity of emission power, calculated from FT-IR measurements, follows in the order of Yeonok, Yanggiseok and Eumgiseok at 40$^{\circ}$C and Yanggiseok, Yeonok and Eumgiseok in such order at 150$^{\circ}$C. As a result of NMR analysis after 20 days in distilled water, the three mineral medicines decreased in the following order; Eumgiseok, Yanggiseok and Yeonok. However, the same minerals decreased in the order of Eumgiseok, Yeonok and Yanggiseok after 80 days. In response temperature, magnetic susceptibility of Yanggiseok and Eumgiseok systematically increased by heating to 25$^{\circ}$C, 100$^{\circ}$C and 700$^{\circ}$C. Magnetic susceptibility of Yeonok shows a decreasing pattern due to heating.
양기와 음기를 보하는 약재로 알려진 양기석과 음기석 및 연옥에 대한 의료적 활용을 파악하고, 광물학적 특성, 분광학적 및 자기적 특성을 규명하기 위하여 X선 형광분석, X-선 회절분석, 주사전자현미경, 적외선 분광분석, 핵자기 공명분석 및 감응자기력을 실시하였다. 광물성 한약으로 사용되는 양기석은 양기석으로 확인되었으뗘, 연옥은 투각섬석으로 구성되었다. 또한, 음기석은 주로 질석으로 구성되며, 소량의 카올리나이트와 할로이사이트를 함유하였다. 사슬형 규산염 중 각섬석군에 속하는 이들 연옥과 양기석은 유사한 범위의 분광학적 특성을 가지며, 연옥은 4$0^{\circ}C$에서 방사에너지가 큰 반면, 양기석은 15$0^{\circ}C$에서 방사에너지가 크다 음기석은 각섬석군의 광물보다 4$0^{\circ}C$와 15$0^{\circ}C$에서 모두 낮은 방사에너지를 나타내었다. 광물성 한약을 증류수에 20일간 침적한 후에 측정한 NMR분석에서의 선폭은 음기석, 양기석, 연옥의 순으로 감소되나, 80일이 경과한 후의 결과는 음기석, 연옥, 양기석 순으로 감소하였다. 양기석과 음기석은 가열 온도가 높아짐에 따라 감응 자기력 값이 대체적으로 증가하고, 연옥은 감소하는 경향을 나타내었다. 광물별로는 상온과 가열시 모두 음기석, 양기석, 연옥의 순으로 감소하였다.