Influence of Filler Composition Ratio on Properties of Both Silica and Carbon Black-Filled Styrene-Butadiene Rubber Compounds

실리카와 카본블랙으로 보강된 SBR 고무 배합물의 특성에 보강제 조성비가 미치는 영향

Influence of the filler composition ratio on cure characteristics and bound rubber content of the compounds and on physical properties of the vulcanizates were studied using both silica and carbon black-filled styrene-butadiene rubber (SBR) compounds with the total filler content of 80.0 phr. The bound rubber content increased slightly with increase of the silica content ratio. The viscosity also increased with increasing the silica content ratio, especially increased steeply after the silica content of 60.0 phr. The cure times obtained with a rheometer, t2, t40, and t90, are increased by increasing the silica content ratio and the cure rate decreased. The delta torque increased with the increased silica content ratio. Variation or the modulus with the silica content ratio showed a decreased trend though the delta torque increased. The tan ${\delta}$ at $60^{\circ}C$ decreased with increased of the silica content ratio.

실리카와 카본블랙으로 보강된 SBR 배합물의 가황 특성과 bound rubber 함량 그리고 가황물의 물성에 보강제의 조성비가 미치는 영향을 연구하였다. 고무 배합물의 보강제 총 함량은 80.0 phr 이다. Bound rubber 함량은 실리카 함랑비가 증가할수록 증가하였고 점도 역시 증가하였는데, 특히 실리카 함량이 60.0 phr 이상일 때는 점도의 증가폭이 두드러지게 높아졌다. 가황시간은 실리카 함량이 증가할수록 느려졌고 가황 속도도 느려졌다. 실리카 함량비가 증가할수록 델타 토크가 증가함에도 불구하고 모둘러스는 감소하는 경향을 보였다. $60^{\circ}C$에서의 tan ${\delta}$ 값은 실리카 함량이 증가할수록 감소하였다.