A Study on the Effects of Additives on the Friction and Wear Properties of PTFE Composite

첨가제에 의한 PTFE 복합재료의 마찰마모 특성에 관한 연구

  • 김용직 (한국해양대학교 대학원) ;
  • 김윤해 (한국해양대학교 기계소재공학부)
  • Published : 2000.08.01

Abstract

This study is mainly concerned with friction and wear properties for the piston ring of non-lubricating air compressor which made of PTFE-polyimide composites. At the PTFE and polyimide alone mixture specimens, PTFE80%-polyimide20%, which shows the lowest mean friction coefficient and specific wear rate at 0.94m/s sliding speed. In case of the specific wear rate, copper30% specimen shows the lowest value of 2.537-5(mm3/Nm) in all specimens. It considered that the friction coefficient is affected by generating speed and quantity of wear film. In case specific wear rate, it is attributed to the fact that the surface hardness of wear film is proportioned to specific wear rate.

본 연구는 공기압축기에 적용되는 피스턴링의 재료에 자기윤활성 재료를 이용할 경우 어떠한 마찰마모 특성을 나타내는가를 비교평가 함으로써 실제 적용여부의 가능성을 확인하였으며, 주요 결과로는 동을 중량비 30% 함유한 시험편이 평균마찰계수 및 비마모량이 가장 적었다. 이는 마찰계수에 직접적인 영향을 주는 마모유동막이 조기에 다량 생성될 경우 낮은 마찰계수와 함께 안정화 효과에 큰 영향을 주며 비마모량은 발생된 마모유동막의 경도와 비례하고 용융마모에 의해 덩어리 형태로 탈락되는 마모분이 가장 적기 때문이라고 생각된다.

Keywords

References

  1. 新材料のトボロジ一 一本潤滑學會
  2. トラィボマテりアル 活用ノ - ト 關口 勇;野呂瀨進;似內昭夫
  3. ねずみ 鑄鐵品 一本工業視格
  4. 表面租さ- 定議及び表示 一本工業視格
  5. 內燃機關講義 全孝重
  6. Sintered Machine Ele-ment Boguslaw Kubick
  7. Wear v.1 no.2 J.T. Burwell Jr.
  8. 한국윤활학회지 v.12 no.3 PTFE-폴리이미드복합재료의 마찰과 마모에 대한 성분비와 온도의 영향 심현해;권오관;이규한;김병환
  9. Stirling Engines G. Walker
  10. トライポロジスト v.40 no.9 久門 輝正;順전 博;河岸 誠;鈴木 宏知
  11. Principle and Applica-tions pf Tribology Bharat Bhushan
  12. トライポロジ-入門 岡本 純三;中山 景次;佐藤 昌夫