Microwave Dielectric Properties of the (1-x)Mg$TiO_3$-xSr$TiO_3$(x=0.02~0.08)Ceramics with Sintering Temperature

소결온도에 따른 (1-x)Mg$TiO_3$-xSr$TiO_3$(x=0.02~0.08)세라믹스의 마이크로파 유전특성

The (1-x)MgTi $O_3$-xSrTi $O_3$(x=0.02~0.08) ceramics were fabricated by the conventional mixed oxide method. The sintering temperature and time were 125$0^{\circ}C$~1375$^{\circ}C$ and 2hours. The structure and microwave dielectric properties were investigated with sintering temperature and composition ratio. From the X-ray diffraction patterns, the cubic SrTi $O_3$and hexagonal MgTi $O_3$structures were coexisted in the (1-x)MgTi $O_3$-xSrTi $O_3$(x=0.02~0.08) ceramics. The dielectric constant($\varepsilon$$_{r}$) was increased and the temperature coefficient of resonant frequency($\tau$$_{f}$)was decreased with addition of SrTi $O_3$. The temperature coefficient of resonant frequency($\tau$$_{f}$) was gradually varied from negative value to positive value with increasing SrTi $O_3$. In the case of 0.96MgTi $O_3$-0.04SrTi $O_3$ceramics sintered at 130$0^{\circ}C$, the dielectric constant, quality factor and temperature coefficient of resonant frequency were 20.5, 5918(at 7.33GHz) and +10ppm/$^{\circ}C$, respectively.y.y.y.