Preparation of Low Density Ceramic Supporter from Fly Ash with Borax and Glass Powder

붕사 및 유리분말을 첨가한 석탄회로부터 저밀도 세라믹 담체의 제조

Low density ceramic supporter was prepared by using fly ash as a starting mterial with borax or glass powders. Also the wheat powders were used by 30 wt% to increase the initial porosity of the supporter. The density of the supporter decreased as the amount of borax increased. The bulk density of $0.79g/\textrm{cm}^3$ and the apparent density of $1.10g/\textrm{cm}^3$ were obtained when the fly ash with 15% of borax was sintered at $1160^{\circ}C$ for 15 minutes. The density also decreased as the plate glass powders past through $212\mu\textrm{m}$ size were mixed. When the fly ash with 12% of glass powder was sintered at $1280^{\circ}C$ for 10 minutes, the bulk and apparent density were $0.90g/\textrm{cm}^3$ and $1.00g/\textrm{cm}^3$, respectively.

석탄회를 출발물질로 사용하고 봉사 및 유리를 첨가하여 저밀도 세라믹 담체를 제조하였다. 또한 성형체의 초기 기공율을 높이기 위하여 밀가루를 30wt% 첨가하였다. 봉사를 첨가함에 따라 겉보기 밀도 및 벌크 밀도가 낮아졌고, 석탄회에 대하여 15wt%의 붕사를 첨가한 결과 $1160^{\circ}C$에서 15분 소결하여 벌크 밀도 $0.79g/\textrm{cm}^3$, 겉보기 밀도 $1.10g/\textrm{cm}^3$인 담체를 얻을 수 있었다. 판유리를 분쇄한 후 212 이하로 체가름한 유리 분말을 첨가하면 붕사와 마찬가지로 밀도가 낮아졌으며, 12wt% 첨가하여 $1280^{\circ}C$에서 10분간 소결한 결과 벌크 밀도 $0.90g/\textrm{cm}^3$, 겉보기 밀도 $1.00g/\textrm{cm}^3$를 얻을 수 있었다.