Fabrication and Chracteristics of Magnetic Sensor using Ceramic Superconductor

산화물 초전도체를 이용한 자기센서의 제작 및 특성

A magnetic field sensor is fabricated with superconducting ceramics of Y-Ba-Cu-O system. The prepared material shows the superconductivity at about 95K. The sensor at liquid nitrogen temperature shows the increase in electrical resistance by applying magnetic field. Actually, the voltage drop across the sensor is changed from zero to a value. more than $100{\mu}V$ by the applied magnetic field. The change in electrical resistance depends on magnetic field. The sensitivity of this sensor is 2.9 ohm/T. The sensing limit is about $1.5{\times}10^{-5}T(=1.5{\times}10^{-1}G)$. The increase in electrical resistance by the magnetic field is ascribed to a modification of the Josephson junctions due to the penetrating magnetic flux into the superconducting material.

YBaCuO계 초전도체로 자기 센서를 제작하였다. 초전도 자기 센서는 약 95K에서 초전도 특성이 나타나며 액체질소온도에서 외부 자계를 인가할 때 전기저항이 증가하였다. 자계 인가로 인해 센서에서 발생되는 전압강하는 0에서부터 $100{\mu}V$이상으로 변화하였다. 전기저항의 변화는 자계에 의존하며, 센서의 감도는 2.9 ohm/T가 된다. 이 센서는 약 $1.5{\times}10^{-5}T(=1.5{\times}10^{-1}G)$까지의 자기를 감지 할 수 있다. 외부자계에 의한 전기저항의 증가는 초전도재료를 관통하는 자속으로 인한 Josephson 접합의 변화에 기인한다.