Abstract
This research is an experimental work of developing a construction material using municipal wastewater sludge as liner and cover materials for waste disposal landfill. Weathered granite soil and flyash, produced as a by-product in the power plant, were used as the primary additives to improve geotechnical engineering properties of sludge. For secondary additives, bentonite and cement were mixed with sludge to decrease the permeability and to increase the shear strength, respectively. Various laboratory test required to evaluate the design criteria for liner and cover materials, were carried out by changing the mixing ratio of sludge with the additives. Basic soil properties such as specific gravity, grain size distribution, liquid and plastic limits were measured to analyze their effects on permeability, compaction, compressibility and shear strength properties of mixtures. Laboratory compaction tests were conducted to find the maximum dry densities and the optimum moisture contents of mixtures, and their effectiveness of compaction in field was consequently evaluated. Permeability tests of variable heads with compacted samples, and the stress-controlled consolidation tests with measuring permeabilities of samples during consolidation process were performed to obtain permeability, and to find the compressibility as well as consolidational coefficients of mixtures, respectively. To evaluate the long term stability of sludges, creep tests were also conducted in parallel with permeability tests of variable heads. On the other hand, for the compacted sludge decomposed for a month, permeability tests were carried out to investigate the effect of decomposition of organic matters in sludges on its permeability. Direct shear tests were performed to evaluate the shear strength parameters of mixed sludge with weathered granite, flyash and bentonite. For the mixture of sludge with cement, unconfined compression tests were carried out to find their strength with varying mixing ratio and curing time. On the other hand, CBR tests for compacted specimen were also conducted to evaluate the trafficability of mixtures. Various test results with mixtures were assessed to evaluate whether their properties meet the requirements as liner and cover materials in waste disposal landfill.
본 연구는 하수처리장 슬러지를 사용하여 매립지의 복토재 및 차수재의 건설재료로 개발하기 위하여 수행한 실험의 분석결과이다. 하수슬러지에 그의 지반공학적 물성증진을 위하여 화강토와 화력발전소의 부산물인 플라이애쉬를 주첨가물로 사용하고 부첨가물로 시멘트 및 벤토나이트를 소정의 혼합비율로 섞어서 각각 전단강도 증진과 투수계수 감소효과를 도모하였다. 주재료인 하수슬러지와 첨가재의 혼합비율을 변화시킨 혼합물에 대하여 다양한 실내실험을 수행하여 복토재 및 차수재의 설계기준의 적합성 여부를 조사하였다. 각 주재료, 첨가재, 혼합물의 비중, 입도분석, 액\ulcorner소성한계 실험을 실시하여 기본물성을 구하고 그들이 투수성, 다짐성, 압축성, 전단강도에 미치는 영향에 대하여 분석하였다. 혼합물에 대하여 실내다짐시험을 실시하여 최대건조단위중량과 최적함수비를 구하고 현장 다짐효율성을 평가하였다. 다짐혼합시료에 대하여 변수두 투수시험을 실시하여 투수계수를 구하는 한편 변수두 투수시험을 하중제어식 압밀시험중에 병행 실시하여 그들의 압밀정수 및 투수계수를 측정하였다. 슬러지의 장기적 안정성과 관련하여 크리프실험을 변수두 투수시험과 함께 실시하였다. 한편, 한달간을 부패시킨 다짐시료에 대하여 투수시험을 실시하여 슬러지내 유기물질 부패에 의한 투수계수에 미치는 영향에 대하여 고찰하였다. 슬러지에 화강토, 플라이애쉬, 벤토나이트를 일정비율로 섞은 혼합물에 대하여 직접전단시험을 실시하여 전단강도정수를 구하였다. 시멘트와 혼합한 슬러지에 대하여 일축압축 강도시험을 실시하여 혼합비와 재령기간에 따른 압축강도 변화를 분석하였다. 한편, 다짐혼합시료에 대하여 CBR시험을 수행하여 그들의 주행성에 대한 평가를 실시하였다. 이와 같은 다양한 실험결과를 종합분석하여 매립지의 차수재 및 복토재로서 사용조건 만족여부를 검토하였다.