Structural and Electrical Properties of Gallium Doped Zinc Oxide Films

Gallium doped zinc oxide(GZO) films were deposited on soda-lime glass substrates without substrate heating $(T_s<50^{\circ}C$) by dc planar magnetron sputtering using GZO ceramic oxide targe with different inert gas (Ar, or Ne). For the GZO films deposited under different total gas pressure $(P_{tot})$, structural and electrical properties were investigated by XRD and Hall effect measurements. Crystallinity of GZO films deposited using Ar was degraded with increase in $(P_{tot})$, suggesting that it was heavily affected by kinetic energy of sputtered Zn particles$(PA_{zn})$ arriving at substrate surface. Whereas, crystallinity of GZO films deposited at lower Ptot than 3.0 Pa using Ne gas was degraded with decrease in $(P_{tot})$. This degradation was considered to be result of film damage caused by the bombardment of high-energy neutrals ($Ne^{\circ}$). On the basis of a hard sphere collision processes, the average final energy of particles (sputtered Zn, $Ar^{\circ}$and $Ne^{\circ}$)arriving at substrate surface were estimated.