Abstract
This study investigated the impact behaviors of the stitched sandwich composites under the low energy impact by the use of drop weight impact tester. These sandwich composites condidted of the glass fabric faces with a urethane foam core. The upper face and the lower face were stitched to combinr through the core thickness direction using the polyester reinforcements. Four types of the stitched sandwich composites, each having a different core thickness, were tested to determine the effects of the core thickness. The impact conditions were changes with the variations of the mass and drop height of the impact tup. The test results showed that the core thickness and the impact condidtions such as the drop height and the mass of the impact tup affected the impact force, the contact time, and the strain behaviors of the stitched sandwich composites. The stitched sandwich composites are able to avert the damage and also maintain the structural integrity even thouth the presence of the damage owing to the through-the-thickness reinforcements. However, it is important to improve the wetting ability of the stitched reinforcements so that the conventional structures are substituted for the stitched sandwich composites effectively.
본 연구에서는 낙하추 방식의 충격시험기를 이용하여 스티칭된 샌드위치 복합재의 저에너지 충격거동을 조사하였다. 스티칭된 샌드위치 복합재는 유리섬유직물의 면재와 우레탄 폼의 코아로 구성되어 있으며 위쪽 면재와 아래쪽 면재는 폴리에스터 보강섬유로 코아의 두께방향을 따라 스티칭하여 일체형으로 결합되어 있다. 이때 코아의 두께가 충격거동에 미치는 영향을 조사하기 위해 코아의 두께를 달리한 네 종류의 스티칭된 샌드위치 복합재를 고려하였다. 스티칭된 샌드위치 복합재에 작용되는 충격조건은 낙하추의 질량과 낙하추의 낙하높이를 조절함으로써 변화시켰다. 연구결과에 따르면 코아의 두께, 낙하추의 낙하높이, 그리고 낙하추의 질량 등의 변화는 스티칭된 샌드위치 복합재에서의 충격하중, 충격체와의 접촉시간, 면재에 형성된 변형율 등에 영향을 미침을 알 수 있었다. 또한 스티칭된 샌드위치 복합재는 스티칭부의 보강효과로 인해 손상을 억제시킬 분 아니라 손상이 발생한 경우에도 구조물로서 역할을 담당할 수 있다. 그러나 스티칭된 샌드위치 복합재를 효율적으로 기존의 구조물에 적용하기 위해서는 스티칭부에서의 수지함침성을 개선할 수 있는 제작공법의 연구가 필요하다.