A Study on the PEG and PCP Binder for Propellant

추진제용 PEG, PCP의 바인더 특성연구

The PEG and PCP have been used as a binder of high energy and minimum smoke propellant. In this study, PEG, PCP 0260, PCP 1270 and mixed PEG/PCP as a prepolymer were used, and also used BTTN/DEGDN and BTTN/TMETN as a plasticizer. Before being cured, the solution viscosity of prepolymer and plasticizer was measured with various contents of PCP in PEG and contents of plasticizer at $20^{\cire}C$~$60^{\cire}C$. The results were shown the increased concentration of PCP enhanced the viscosity of solution due to the hydrogen bond of PCP, and the increased contents of plasticizer undoubtedly decrease the viscosity of solution. The cured binders were tested for mechanical properties and measured for glass transition temperature with various concentration of PCP in PEG and contents of plasticizer. The increased concentration of PCP has shown better mechanical properties. This results were attributed to the H-bond. Also, the glass transition temperature was lowered with the higher contents of PCP Finally, with the higher content of PCP in PEG, the better mechanical properties and the lower glass transition temperature and the higher viscosity of solution were shown.

고에너지 및 무연 추진제의 바인더 중 프리폴리머로 PEG 및 PCP가 널리 사용되어왔다. 본 연구에서는 PEG 프리폴리머에 PCP0260 및 PCP1270을 혼합 사용한 경우와 PCP0260, PCP1270, PEG만을 각각 단독으로 사용한 경우에 또 가소제로는 BTTN/DEGDN, BTTN/TMETN계를 사용하여 PEG/ PCP의 함량 변화, Pl/Po의 함량 변화에 대한 점도 변화를 온도에 따라서 고찰하였고, 경화된 바인더로는 PEG/PCP의 함량 변화, Pl/Po의 함량 변화에 따라 기계적 특성, 유리전이 온도를 고찰하였다. 그 결과 PCP의 함량이 증가함에 따라 점도는 상승하나, 유리전이 온도가 낮아지므로 저온물성이 좋아지며, 기계적 특성이 우수한 장점을 지니고 있다. 또한 TMETN은 DEGDN에 비하여 유리전이 온도 및 점도의 상승을 보이는 단점을 나타내고 있다.