Effect of Polycaprolactone on the Mechanical Properties of PEG/HMX Propellant

Polycaprolactone이 PEG/HMX 추진제의 기계적 성질에 미치는 영향

Mechanical properties of polyethyleneglycol(PEG)/cyclo-tetramethylene tetranitramine(HMX) propellant were studied by adding polycaprolactone(PCP) and silane derivatives as coupling agent. Mechanical properties of the propellant were enhanced by increasing the content of PCP which was partially replaced with PEG. PCP/HMX propellant showed 17% increase in maximum tensile strength and 59% increase in elongation compared to those of PEG/HMX propellant. However, as the content of PCP was increased, the hydrolytic stability of this propellant was found to be deteriorated due to the ester group of PCP by measuring hardness drop of cured propellant and swell ratio difference of PEG/PCP binder stored at $40^{\cire}C$ and 90% relative humidity. Hardness of the PEG/PCP/HMX propellant was decreased with increasing triethoxysilyl propionitrile(TESPN) and dinitrosalicylic acid (DNSA) content from accelerated aging at $60^{\cire}C$.

Polycaprolactone (PCP)과 coupling agent로 silane 유도체를 polyethylene glycol(PEG)/cyclo-tetramethylene tetranitramine(HMX) 추진제에 첨가하였을 때 추진제의 기계적 특성 변화를 연구하였다. PEG의 일부를 Polycaprolactone(PCP)으로 대체 사용하면 추진제의 기계적 성질은 증가하였으며, PCP/HMX 추진제는 PEG/HMX보다 최대 인장 강도가 17%, 최대 응력하의 신율은 59% 증가하였다. 그러나 PCP함량이 증가할수록 수분에 대한 안정성은 저하됨을 $40^{\cire}C$의 온도와 90% 상대 습도 분위기에서 보관된 추진제의 경도 변화와 PEG/PCP바인더의 부피 팽윤 실험에 의해 알 수 있었다. 또한 PEG/PCP/HMX 추진제를 $60^{\cire}C$에서 가속 노화시키면 triethoxysilyl propionitrile(TESPN)과dinitrosalicylic acid((DNSA) 함량이 증가할수록 추진제의 경도가 감소하는 것으로 나타났다.