Abstract
It is well known that new tissue or blood vessel is grown into a porous calcium phosphate ceramics used as a bone graft substitute due to their excellent biocompatibility. In this study, the most chemically stable porous $\beta$-crystalline form in various forms of calcium metaphosphate, Ca(PO$_3$)$_2$is prepared by the controlled thermolysis of monocalcium phosphate, Ca(H$_2$PO$_4$)$_2$.The diameter of cylindrical pores formed during cooling was controlled by a holding time at the melting point of a monocalcium phosphate and by the change of a crystallization temperature, to obtain the most appropriate size (about 200$\mu$m) of pores for the application of bone substitutes and matricuts. It was observed that the increasing holding time at the melting point of monocalcium phosphate results in the decreases of cylindrical pore sizes.
다공질 칼슘 인산계 세라믹스는 생체 친화성이 우수하여 경조직 대체재료로 사용되었을 때 새로운 인체 조직이나 실핏줄이 쉽게 성장해 들어가는 것으로 알려졌다. 본 연구에서는 여러 결정구조를 갖는 칼슘 메타인산염 중 화학적으로 가장 안정한 $\beta$형의 다공질 칼슘 메타인산염을 칼슘 인간염, Ca(H,PO,),를 열분해 시켜 제조하였다. 칼슘 인산염의 용융상태에서 냉각 중 생성되는 원통형 기공의 크기는 경조식 대체재료나 매트릭스로 사용되기 적절한 200$\mu$m로 만들기 위하여 응용온도에서 유지시간 또는 결정화 온도를 조절하였다. 본 실험에서 칼슘 인산염의 응용온도에서 유지시간을 길게 함에 따라 원통형 기공의 크기가 작아졌다.