초록
In this paper, we investigate frequency dependance of inductance of FeCoB amorphous magnetic films. $(Fe_{1-x}Co_x)_{79}Si_2B_{19}$ was used as the basic composition of amorphous magnetic film having near zero magnetostriction. The amorphous magnetic films were fabricated with x=0.94 and x=0.95 by using sputtering method at high frequency. The films were anneald under non-magnetic field and near crystallization temperatures(30min at $280^{\circ}C$, 30min and 1hr at $400^{\circ}C$, respectively). As the results of the experiments with the fabricated films, the lowest coercive force was 0.084[Oe] at 400[W] of the input power and the crystallization temperature was $360^{\circ}C$ . In the case 30min at 40$0^{\circ}C$ the inductance value in the low frequency with x=0.95 was higher by 488% than that with x=0.94. The quality factor Q was below 0.7 for all samples. We obtained the highest quality value at 400[KHz] with 30min at $280^{\circ}C$ and x=0.94. The value was about 0.62. Also, the quality factor value was about 0.35 at 1[MHz] with 30min at $280^{\circ}C$ and x=0.95.