The Preparation of NiCuZn Ferrite Slurry Using the Water Mixed Binder System

수계 바인더를 이용한 NiCuZn Ferrite의 슬러리 제조

Surface mount technology is the biggest theme in the area of deιIronic component. To miniatunze an electronic component, s such as ferrite chip inductor, the cer뼈lic wet process for green-sheet lamination and/or screen printing method through a s solvent medium system is widely used. The preparation and characterization of NiCuZn Ferrite (NCZF) shurry and the green s sheet using the water mixed binder system has been studied. The 21 vol% of NCZF slurry was prepared by a ball milling. The p polyacrylic vinyl copolymer (Mw; 60,000) was used as a binder. Th$\xi$ mixture of distilled water, isopropyl alcohol (IPA) and 2l butoxy ethanol was used as a dispersion medium. The water content of medium varied from about 40% to 80%. As the results. Thc disp$\xi$rston stability of the NCZF slurry was attributed to the free polymer rather than the electrostatic force of the particle. T The viscosity of the NCZF slurry was greatly depended on the ratio of water content in the medium.

오늘날 전자부품 산업에 실장기술은 크게 각광을 받고 있다. 페라이트 칩인덕터와 같이 전자부품의 소형화를 위해서는, 쉬트 적층법이나 스크린 인쇄법 등을 위하여 유기용매를 사용하는 세라믹 습식공정이 널리 사용되고 있다. 본연구에서는 물이 혼합된 용매계를 이용한 NiCuZn Ferrite(NCZF) 슬러리와 그린쉬트의 제조 및 평가에 관한 연구를 하였다. 볼밀링에 의하여 21 vol%의 NCZF 슬러리를 제조하였으며, polacrylic vinyl copolymer를 바인더로서 사용하였다. 용매로서는 isopropyl alcohol과 2-butoxy ethanol에 40∼80% 물을 혼합하여 사용하였다. 그 결과, NCZF 슬러리의 분산안정성은 입자의 정전기적 힘보다는 free polymer에 의해 나타났으며, 슬러리의 점성은 용매중의 물함량에 크게 의존하였다.