Abstract
We investigated the effects of the powder characteristics of various domestic iron oxides (${\alpha}Fe_2O_3$) on the magnetic properties of Sr-ferrites The particle size and the distribution of iron oxides were classified hy three different rerinning methods, and greatly a affected on the magn$\xi$tic prope$\pi$ies and the mmphology of Sr-ferntes. The agglomeration of Ruthner iron oxides and the large particles of Chemirite (CY) above $0.80{\mu}\textrm{m}$ were degraded the prope며es of Sr-fcrrites. The optimal magnetic prope$\pi$ies of Srt territes, showing 68.2 emu/g of saturation magnetization and 4300 Oe of intrinsic coerClvity, were achieved at the following c conditions; Chemirite (P2EP) iron oxides of $0.14{\mu}\textrm{m}$ molar ratio of 5.8. and calcination of $1150^{\circ}C$/1 hr.
다양한 hard ferrite용 국산 산화철(${\alpha}Fe_2O_3$)의 분체특성이 Sr-ferrite의 자기특성에 미치는 영향을 조사하였다. 산화철의 평균입도와 입도분호는 철강 냉연공장의 염산폐액 정제방법에 따라 서로 구분되었으며, Sr-ferrite의 자기특성과 미세조직에 큰 영향을 주었다. Ruthner 산화철의 응집현상은 Sr-ferrite의 포화자화를 감소시켰으며, Chemirite(CY) 산화철의 $0.80{\mu}\textrm{m}$이상의 조대한 입자는 Sr-ferrite의 고유보자력을 감소시켰다. 평균입도가 $0.14\mu\textrm{m}$로 가장 작은 Chemirite 포항2냉연(EP) 산화철을 사용하여, 5.8mol, $1150^{\circ}C$/1시간의 하소조건에서 제조된 Sr-ferrite는 포화자화가 68.2emu/g, 고유보자력이 4300Oe인 최적의 자기특성을 나타내었다.