Analysis of Pore Structure for Porous Body with Coal Fly ash and Clay
석탄회-점토계 다공체의 기공구조 분석
Abstract
Porous body was prepared from coal fly ash 70 wt%0clay 30 wt% slip using DCC(Direct Coagulated Casting) method. Effect of the specific gravity of the slip on the pore size and distribution of the sintered body was examined by the SEM observation of microstructure and mercury porosimetry measurement of the pore size distribution. Average pore size of the porous sintered body was about 2.5μm for all slips with specific gravity of 1.55, 1.60 and 1.65g/cm3, respectively. Sintered body prepared from the slip of specific gravity of 1.60g/cm3 have the narrowest pore size distribution. slip of specific gravity of 1.55g/cm3 shows broader pore size distribution due to slow gellation process. Slip of specific gravity of 1.65g/cm3 required large amount of deflocculant and showed large variation of the viscosity with addition of coagulant which resulted in very unstable slip properties.
석탄회 70 wt%-점토 30wt%인 슬립으로부터 DCC(Direct Coagulation Casting)법을 이용하여 다공체를 제조하였다. 각각 1.55, 1.60, 1.65g/cm3의 비중을 갖는 슬립으로부터 제조한 다공체의 미세구조 관찰 및 기공크기 분포 측정을 통해 슬립의 비중이 기공크기 및 분포에 미치는 영향에 대해서 연구하였다. 슬립의 비중에 관계없이 평균기공의 크기는 약 2.5μm이었으며, 1.60g/cm3의 비중을 갖는 슬립으로부터 제조된 다공체의 미세구조 및 기공분포가 가장 균일하였다. 슬립비중 1.55g/cm3인 경우에는 고체의 양이 작아 겔화의 진행이 느려 기공분포가 넓어졌으며, 비중 1.65g/cm3인 슬립은 해교제의 첨가량이 많아 응집제 첨가시 점도의 변화가 매우 컸으며 불안정한 슬립 특성을 보였다.
Keywords