Abstract
We investigated the structural and dielectric properties of PZT(20/80)/PZT(80/20) heterolayered thin films that fabricated by the alkoxide-based Sol-Gel method. PZT(20/80)/PZT(80/20) heterolayered thin films were spin-coated on the Pt/Ti/SiO$_2$/Si substrate with PZT(20/80) film of tetragonal structure and PZT(80/20) film of rhombohedral structure by turns. Each layers were dried to remove the organic materials at 30$0^{\circ}C$ for 30min and sintered at $650^{\circ}C$ for 1hr. This procedure was repeated several times to form PZT(20/80)/PZT(80/20) heterolayered films and thickness of the film obtained by one-times of drying/sintering process was approximately 80-90nm. PZt-1, 3, 5 films with top layer of PZT(20/80) film of tetragonal structure showed fine grain structure and PZT-2, 4, 6 films with top layer of PZT(80/20) film of rhombohedral structure showed the dense grain microstructure without rosette-type. Dielectric constant and dielectric loss of the PZT-6 film were approximaterly 1385 and 3.3% respectively. Increasing the number of coatings remanent polarization was increased and coercive field was decreased and the values of the PZT-6 film were 8.13$\mu$C/cm$^2$and 12.5kV/cm respectively.