• Electrical & Electronic Materials
• /
• v.10 no.10
• /
• pp.983-988
• /
• 1997

We investigated the structural and dielectric properties of PZT(20/80)/PZT(80/20) heterolayered thin films that fabricated by the alkoxide-based Sol-Gel method. PZT(20/80)/PZT(80/20) heterolayered thin films were spin-coated on the Pt/Ti/SiO$_2$/Si substrate with PZT(20/80) film of tetragonal structure and PZT(80/20) film of rhombohedral structure by turns. Each layers were dried to remove the organic materials at 30$0^{\circ}C$ for 30min and sintered at $650^{\circ}C$ for 1hr. This procedure was repeated several times to form PZT(20/80)/PZT(80/20) heterolayered films and thickness of the film obtained by one-times of drying/sintering process was approximately 80-90nm. PZt-1, 3, 5 films with top layer of PZT(20/80) film of tetragonal structure showed fine grain structure and PZT-2, 4, 6 films with top layer of PZT(80/20) film of rhombohedral structure showed the dense grain microstructure without rosette-type. Dielectric constant and dielectric loss of the PZT-6 film were approximaterly 1385 and 3.3% respectively. Increasing the number of coatings remanent polarization was increased and coercive field was decreased and the values of the PZT-6 film were 8.13$\mu$C/cm$^2$and 12.5kV/cm respectively.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.54 no.1
• /
• pp.13-17
• /
• 2005

The Pb(Zr/sub 0.52/Ti/sub 0.48/)O₃/(Ba/sub 0.6/Sr/sub 0.4/)TiO₃[PZT/BST] heterolayered thin films were deposited on Pt/Ti/SiO₂/Si substrates by using the RF sputtering method with different RF power. The PZT/BST heterolayered thin films had the tetragonal structure of the PZT phase and BST phase. Increasing the RF power. the intensity of the PZT (100), (110) peaks and BST (111) peaks were decreased and the intensity of the BST (100), (110) peaks were increased. The thickness ratio of the top layered BST thin film and the bottom layered PZT thin film was 2 to1. The atomic concentration of the Ba, Sr, Pb. Zr, Ti atoms were constant in the PZT thin films and BST thin films, respectively. The Pt atom was diffused to the PZT region in the PZT/BST heterolayered thin films deposited at condition of 60[W] RF power. Increasing the frequency, dielectric constant and loss of the PZT/BST heterolayered thin films were decreased. The dielectric constant and loss of the PZT/BST heterolayered thin films deposited with RF power of 90[W] were 406 and 3%, respectively.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.7
• /
• pp.514-520
• /
• 1999

Ferroelectric PZT(30/70)/PZT(70/30) heterolayered thin films were fabricated by spin-coating method on the $Pt/Ti/SiO_2Si$ substrate alternately using(30/70) and PZT(70/30) alkoxide solutions prepared by sol-coating method. The coating and heating procedure was repeated six times to form PZT heterolayered films, and thickness of the film obtained by one-times drying/sintering process was about 40-50 nm. All PZT heterolayered films, showed dense and homogeneous structure without the presence of rosette sturctrue. The relative dielectric constant, remanent polarization and leakage current density of PZT heterolayered films were superior to those of single composition PZT(30/70) and PZT(70/30) films, and those values for the PZT-6 film were 975, $21 \muC/cm^2\; and\; 8\times10^{-9}\; A/cm^2$, respectively. And the PZT-6 heterolayered film showed fairly good fatigue characteristics of remanent polarization and coercive field after application of $10^8$ switching cycles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.260-261
• /
• 2005

The heterolayered thick/thin structure consisting of $Pb(Zr_{0.52}Ti_{0.48})O_3$ and $BaTiO_3(BT)$ were fabricated by a sol-gel process. PZT powders, prepared by the sol-gel method, were mixed with an organic vehicle and the PZT thick films were fabricated by the screen printing techniques on alumina substrate with Pt electrodes. The microstructural and dielectric characteristics of the stacked heterolayered PZT/BT/PZT films were investigated by varying the number of coating $BaTiO_3$ layers. The existence of a $BaTiO_3$ layer between the PZT thick films of the tri-layer $Pb(Zr_xTi_{1-x})O_3/BaTiO_3/Pb(Zr_xTi_{1-x})O_3$thick/thin/thick film can greatly improve the leakage current properties of the PZT thick films. The average thickness of a PZT(5248)/$BaTiO_3$ heterolayered thick/thin film was 25$\mu$m. The relative dielectric constant and dielectric loss of the PZT(5248)/$BaTiO_3$-3 heterolayered thin film coated three times were 1087 and 1.00% at 1[MHz].

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1229-1231
• /
• 1997

In this work, PZT(20/80)/(80/20) heterolayered thin film that has the tetragonal and rhombohedral structure was fabricated by Sol-Gel method spin-coated on the Pt/Ti/$SiO_2$/Si substrate by turns. The thickness of PZT-1 film obtained by six-times of drying/sintering process was about 480[nm]. This procedure was repeated several times to form PZT heterolayered thim film. PZT-5 thin films with top layer of tetragonal PZT(20/80) thin film showed dense grain structure and PZT-6 thin film with top layer of rhombohedral PZT(80/20) thin film showed the microstructure without rosette. Dielectric constant increased with increasing the number of coatings, and it was about 13S5 at PZT-6 thin film. Dielectric loss was not depend on the number of coatings.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.109-112
• /
• 1999

The PZT(10/90)/(90/17) heterolayered thin films were fabricated by the spin-coaling on the Pt/Ti/SiO$_2$/Si substrate using the PZT(10/90) and PZT(70/10) metal alkoxide solutions. The effect of heterolayered thin films on the ferroelectrics and electrical properties have been investigated. The lower PZT layers provided the nucleation site for the formation of a perovskite phase of the upper PZT films. Dielectric constant increased with increasing the number of coatings, and it was about 569.9 at PZT-6 heterolayered films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.607-610
• /
• 2004

The Pb $(Zr_{0.52}Ti_{0.48})O_3/(Ba_{0.6}Sr_{0.4}TiO_3$ [PZT(52/48)/BST(60/40)] heterolayered thin films were fabricated on the Pt/Ti/$SiO_2$/Si by RF sputtering method. The structural properties of the PZT(52/48)/BST(60/40) heterolayered thin films were investigated with Ar/$O_2$ ratio condition. All the PZT(52/48)/BST(60/40) heterolayered thin films had shown the PZT(111), (200) and BST(200) Peaks of the tetragonal structure. Increasing the Ar/$O_2$ ratio, the average roughness was increased. The thickness ratio of the to the PZT and BST thin film was 1:2. In the case of the PZT(52/48)/BST(60/40) heterolayered thin films with Ar/$O_2$ ratio of 80/20, the average roughness was 3.4 [nm].

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.2
• /
• pp.98-102
• /
• 2000

Ferroelectric PZT heterolayered thin films were fabricated by spin coating method on the Pt/Ti/SiO2/Si substrate using PZT(10/90) and PZT(90/10) m7etal alkoxide solutions. All PZT heterolayered films showed a homogeneous grain structures without presence of rosette structure. It can be assumed that the lower PZT layers played a role of nucleation site for the formation of the upper PZT layer. Pb-deficient PZT phase was formed at PZT/Pt interface due to the diffusion of Pb element into a Pt bottom electrode. The relative dielectric constant and the dielectric loss of the PZT-6 film were 567 and 3.6%, respectively. Increasing the number of coatings, remanent polarization and coercive field were decreased and the values of the PZT-6 heterolayered film were $7.18\muC/cm^2$ and 68.5kV/cm, respectively. Leakage current densities were increased with increasing the number of coatings, and the value of the PZT-4 film was about $7\times10-8A/cm^2$ at 0.05MV/cm.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1621-1623
• /
• 2004

The $Pb(Zr_{0.52}Ti_{0.48})O_3/(Ba_{0.6}Sr_{0.4})TiO_3$ [PZT(52/48)/BST(60/40)] heterolayered thin films were deposited on Pt/Ti/$SiO_2$/Si substrates by using the RF sputtering method with RF powers of 60,70,80,90[W]. All thin films showed the peaks of the tetragonal phase. Increasing the RF power, dielectric constant and loss of the PZT(52/48)/BST(60/40)] heterolayered thin films were decreased. The thickness ratio of PZT and BST thin films was 1/1. The relative dielectric constant and the dielectric loss of the PZT(52/48)/ BST(60/40) heterolayered thin films were 562 and 13%, respectively.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1771-1773
• /
• 1999

Ferroelectric PZT(10/90)/(90/10)heterolayered thin films were fabricated by the alkoxide-based Sol-Gel method Electric and dielectric properties of PZT(10/90)/(90/10) heterolayered thin films have been investigated, focusing on the effect of PZT/PZT and PZT/electrode interface on the heterolayered films. Dielectric constant increased with increasing the number of coatings. Increasing the number of coatings, remanent polarization and coercive field were decreased and the values of the PZT-6 heterolayered thin films deposited on Pt/Ti/$SiO_2$/Si were $7.18{\mu}C/cm$, $68.5kV/cm^2$, respectively. Leakage current, densities were increased with increasing the number of coatings, and the value of the PZT-4 film deposited on the Pt/Ti/$SiO_2$/Si substrate was about $7{\times}10^{-8}A/cm^2$ at 0.05MV/cm.