ELECTRON MICROSCOPIC STUDY OF RESIN-DENTIN HYBRID ZONE PRODUCED BY THE MOISTENING OF ACID CONDITIONED DENTIN SURFACE

산 표면처리 후 상아질 표면의 습윤이 하이브리드층 형성에 관한 전자현미경적 연구

The effect of moistening and air-drying of acid-conditioned dentin before priming on the formation of resin-dentin hybrid zone was investigated, Freshly extracted human molars were used and divided at random into 5 groups, Groups 1 - 3 consisted of specimens conditioned with 10 % phosphoric acid for 20 seconds; Group 1 served as a control in which the conditioned dentin was simply blot-dried with a damp facial tissue; Group 2 was air dried for 30 seconds ; Group 3 was air dried for 30 seconds and immediately remoistened for 10 seconds with air-water syringe. and then the specimen was blot-dried with a damp facial tissue. Groups 4-5 were not acid conditioned ; In group 4, the smear layer on the dentin was blot dried before primer placement; Group 5 was air dried only for 30 seconds, The acetone-based primer and bonding agent of All Bond 2 (Bisco. Inc., USA) and composite resin (Z-100, 3M Dental products, USA) were applied for acid conditioned dentin and non-conditioned dentin. The morphologic ultrastructure of resin-dentin hybrid zone was examined by the use of SEM and TEM. and the existence of inorganic material and analysis of Ca/P weight-percent ratio in the resin-dentin hybrid zone were revealed by the EDAX, The results were as follows : 1. In the moistened specimens from acid-conditioned groups, the resin penetrated about 3-$4{\mu}m$ into dentin and the denatured collagen smear layer was not present at the surface. The resin tag was formed to a thickeness of 3-$4{\mu}m$ at the upper part of dentinal tubule and compactively connected to each other by means of many lateral branching. 2. In the air-dried specimens from acid-conditioned groups, the resin penetrated about 2.0-$2.5\;{\mu}m$ into dentin and an upper thin black layer to a thickness of 30-35nm was identified between adhesive resin and demineralized collagen layer. The resin tag to have a diameter of $2.5{\mu}m$ was formed at the upper part of dentinal tubule. However the funnel shape of the tag was not notable compared to the moistened specimens. 3. In the remoistened specimens from acid conditioned groups, the resin penetrated about 2.0-$2.5{\mu}m$ into dentin and an upper black layer was not present. The resin tag at the upper part of dentinal tubule was formed less than $2{\mu}m$ and was weakly connected to each other by means of few lateral branching. 4. In the non-conditioned groups, the smear layer was formed to a thickness of $0.5{\mu}m$ at dentin surface. However, the resin-dentin hybrid zone was not identified by TEM. The evidence of resin penetration into intertubular and intratubular dentin did not show. 5. All the acid-conditioned groups showed that the detected calcium and phosphorus weight percent ratios at the $2{\mu}m$ upper portion from the resin-dentin interface into the resin were much higher than that at the $2{\mu}m$ lower portion from the resin-dentin interface to dentin. (P<0.01).